The purpose of this study was to evaluate the microtensile bond strength (µTBS) and Knoop hardness number (KHN) of a novel experimental light-cured resin cement (HL). Eighteen flat dentin surfaces of human molars were polished using #600 SiC paper and bonded to CAD/CAM resin blocks with the respective resin cements and composites: HL, Panavia V5 (PV), and Clearfil AP-X (AP). All specimens were stored in distilled water at 37 °C for 24 h and 7 days. Scanning electron microscope (SEM) and energy dispersive X-ray (EDX) observations were performed to evaluate filler morphology and to detect the elements. The resin cements had a significant effect on the immediate µTBS (F = 22.59, p < 0.05) and after water storage µTBS (F = 22.83, p < 0.05). Significant differences (p < 0.05) in the KHN between the tested materials were observed, and HL indicated the highest KHN when compared with PV. HL showed a combination of the regular-shaped filler and spherical-shaped filler within the matrix. Silicon was detected in HL from the EDX evaluation. HL exhibited better bonding performance and polymerization, which may have contributed to the improvement of the adhesive strength.

This study aimed to evaluate the stick behavior and performance of an adhesive for facial prostheses on esthetics and strength. Forty subjects participated in this study. Mimic the skin was fabricated, applied to one cheek of each subject using only medical adhesive, and to the opposite cheek using the same medical adhesive and an overlying film dressing. Ninety-five percent of subjects reported that the silicone prosthesis with film dressing did not peel off and was less noticeable. The combination of medical adhesive and film dressing provided stronger adhesion and better esthetics compared to medical adhesive alone.