This research investigates the possibility of using high-density polyethylene (HDPE) plastic waste to improve the properties of asphalt concrete pavement. HDPE plastic waste contents of 1, 3, 5, and 7% by aggregate weight were used. HDPE plastic waste=stabilized asphalt concrete pavement (HDPE-ACP) was evaluated by performance testing for stability, indirect tensile strength, resilient modulus (MR), and indirect tensile fatigue (ITF). In addition, microstructure, pavement age, and CO₂ emissions savings analyses were conducted. The performance test results of the HDPE-ACP were better than those without HDPE plastic waste. The optimum HDPE plastic waste content was 5%, offering the maximum MR, ITF, and pavement age. Scanning electron microscope images showed that the excessive HDPE plastic waste content of 7% caused a surface rupture of the sample. Improvements in the pavement age of the HDPE-ACP samples were observed compared with the samples with no HDPE plastic waste. The highest pavement age of the HDPE-ACP sample was found at an HDPE plastic waste content of 5% by aggregate weight. The CO₂ emissions savings of the sample was 67.85 kg CO₂-e/m³ at the optimum HDPE plastic waste content.

This research investigated high calcium fly ash geopolymer stabilized recycled concrete aggregate (RCA-FAG) as pavement base material. The effect of recycled concrete aggregate (RCA):high calcium fly ash (FA) ratios, sodium silicate (Na₂SiO₃):sodium hydroxide (NaOH) ratio, and curing time on the unconfined compressive strength (UCS) and scanning electron microscope (SEM) properties of RCA-FAG samples were evaluated. The maximum dry unit weight of the RCA-FAG sample was 20.73 kN/m³ at RCA:FA ratio of 80:20 and Na₂SiO₃:NaOH ratio of 60:40. The 7-d UCS of RCA-FAG samples increased as the FA content and Na₂SiO₃:NaOH ratio increased. The 7-d UCS of the RCA-FAG sample was better than that of the RCA with no FA because FA particles filled in RCA particles, resulting in a dense matrix. The 7-d UCS of RCA-FAG samples passed the 7-d UCS requirement for the low-traffic road. All ingredients met the 7-d UCS requirement for the high-traffic road except the sample with RCA:FA of 100:0 and Na₂SiO₃:NaOH of 50:50 and 60:40. The 7-d SEM images indicated that spherical FA and RCA particles are bonded together, resulting in the dense matrix for all Na₂SiO₃:NaOH ratios. The proposed equation for predicting the UCS of RCA-FAG offered a good coefficient of correlation, which is useful in designing pavement base material from RCA-FAG material.