The use of concrete in road construction has grown over the past decade due to the material’s great durability. However, concrete has poor tensile strength, ductility, and energy absorption. This paper aims to investigate the utilization of plastic waste, namely polypropylene (PP), to create a novel fiber to enhance the engineering properties of fiber reinforced concrete (FRC), an eco-friendly concrete that can reduce environmental problems. The 28-day design strengths of 28 and 32 MPa were used in this study because the compressive strength requirements for concrete footpaths and pavement specified by Austroads and the Department of Highways, Thailand, were at least 25 and 32 MPa, respectively. The fiber (F) was a mixture of virgin PP and recycled PP (RPP). The study used F contents of 0.25, 0.50, 0.75, and 1% by weight of cement and PP:RPP ratios of 100:0, 75:25, 50:50, 25:75, and 0:100. The compressive strength, flexural strength, leaching, and CO₂ emissions savings of FRC were evaluated. Improvements in the compressive strength, flexural strength, and toughness of the samples with F were observed in comparison to the control concrete samples for all design strengths. All mixtures met the compressive strength requirements for concrete footpaths, except for F contents of 0.75 and 1% and a PP:RPP ratio of 0:100. By contrast, the 32 MPa FRC samples with F contents of 0.25 and 0.5% and all PP:RPP ratios met the requirements for rigid pavement. From an environmental perspective, the heavy metal contaminants of the 32 MPa FRC sample were within the allowable limits for all mixtures. Regarding incineration disposal, the maximum CO₂ emissions savings of 28 MPa and 32 MPa FRC with an F content of 0.5% and a PP:RPP ratio of 0:100 were 1.0 and 1.11 kg CO₂-e/m³, respectively. This research will enable plastic waste, traditionally destined for incineration and landfill disposal, to be used as a sustainable fiber in the construction industry.

This research investigates the possibility of using high-density polyethylene (HDPE) plastic waste to improve the properties of asphalt concrete pavement. HDPE plastic waste contents of 1, 3, 5, and 7% by aggregate weight were used. HDPE plastic waste=stabilized asphalt concrete pavement (HDPE-ACP) was evaluated by performance testing for stability, indirect tensile strength, resilient modulus (MR), and indirect tensile fatigue (ITF). In addition, microstructure, pavement age, and CO₂ emissions savings analyses were conducted. The performance test results of the HDPE-ACP were better than those without HDPE plastic waste. The optimum HDPE plastic waste content was 5%, offering the maximum MR, ITF, and pavement age. Scanning electron microscope images showed that the excessive HDPE plastic waste content of 7% caused a surface rupture of the sample. Improvements in the pavement age of the HDPE-ACP samples were observed compared with the samples with no HDPE plastic waste. The highest pavement age of the HDPE-ACP sample was found at an HDPE plastic waste content of 5% by aggregate weight. The CO₂ emissions savings of the sample was 67.85 kg CO₂-e/m³ at the optimum HDPE plastic waste content.

This research investigated high calcium fly ash geopolymer stabilized recycled concrete aggregate (RCA-FAG) as pavement base material. The effect of recycled concrete aggregate (RCA):high calcium fly ash (FA) ratios, sodium silicate (Na₂SiO₃):sodium hydroxide (NaOH) ratio, and curing time on the unconfined compressive strength (UCS) and scanning electron microscope (SEM) properties of RCA-FAG samples were evaluated. The maximum dry unit weight of the RCA-FAG sample was 20.73 kN/m³ at RCA:FA ratio of 80:20 and Na₂SiO₃:NaOH ratio of 60:40. The 7-d UCS of RCA-FAG samples increased as the FA content and Na₂SiO₃:NaOH ratio increased. The 7-d UCS of the RCA-FAG sample was better than that of the RCA with no FA because FA particles filled in RCA particles, resulting in a dense matrix. The 7-d UCS of RCA-FAG samples passed the 7-d UCS requirement for the low-traffic road. All ingredients met the 7-d UCS requirement for the high-traffic road except the sample with RCA:FA of 100:0 and Na₂SiO₃:NaOH of 50:50 and 60:40. The 7-d SEM images indicated that spherical FA and RCA particles are bonded together, resulting in the dense matrix for all Na₂SiO₃:NaOH ratios. The proposed equation for predicting the UCS of RCA-FAG offered a good coefficient of correlation, which is useful in designing pavement base material from RCA-FAG material.

This research investigated the unit weight and unconfined compressive strength (UCS) of cellular lightweight high-calcium fly ash geopolymer and cement-stabilized soft Bangkok clay (CLFAG-OPC stabilized SC) as potential lightweight embankments and backfill materials. The investigated parameters included the soft clay:fly ash (SC:FA) ratio (50:50 to 90:10), ordinary Portland cement (OPC) content (0%-3%), water content (1.5LL-3.0LL), liquid alkaline content (L) (0.6FA to 1.5FA), NS:NH ratio (0.5-3), NH concentration (8 M), air foam content (Ac) (0%-150% by SC volume), and curing time (7-90 days). The results indicated that the SC:FA ratio, OPC content, water content, NS:NH ratio, L content, and Ac significantly influenced both the unit weight and UCS of samples. Increasing water content, L content, and Ac generally reduced unit weight, except when influenced by FA content, OPC content, and the NS:NH ratio. The optimal composition for maximum UCS was achieved with an SC:FA ratio of 50:50, OPC content of 3%, water content of 2.0LL, NS:NH ratio of 1, L content of 0.6FA, and 0% Ac. A predictive equation for unit weight was proposed using phase diagrams. Additionally, mix design charts were shown to be valuable tools for calculating the unit weight and UCS, demonstrating their effectiveness for lightweight embankment and backfill applications.