The partial pressures of saturated vapor of the components in the Se–Te system are determined and presented in the form of temperature–concentration dependences from which the boundaries of the melt–gas phase transition are calculated at atmospheric pressure and vacuums of 2000 and 100 Pa. The existence of azeotropic mixtures is revealed. It is found that the points of inseparably boiling melts correspond to 7.5 at % of Se and 995°C at 101325 Pa, 10.9 at % at 673°C and 19.5 at % at 522°C in vacuums of 2000 and 100 Pa, respectively. A complete state diagram is constructed, including the fields of gas-liquid equilibria at atmospheric and low pressures, the boundaries of which allow us to assess the behavior of selenium and tellurium upon distillation fractionation.

The values of partial pressure of saturated vapor of the constituents of the Те–S system are determined from boiling points. The boundaries of the melt–vapor phase transition at atmospheric pressure...

The heterogeneity and local distribution of elements are established as a result of the study of nonferrous metals distribution and the composition of domestic wastes processing concentrate containing 20–40% copper, 40–50% brass, 20–28% zinc and up to 1% aluminium. Metals are mainly concentrated in granules of three types: zinc-based, copper-based and copper–zinc alloy, i.e., brass. The phase composition of these granule types and their structure are determined. Zinc granules are covered with a refractory oxide shell. A distillation processing method for such raw materials based on full state diagrams, including the phase transition of melting pairs of double systems of copper and tin with zinc and lead, is offered. The possibility of a rather complete zinc distillation (over 90%) with the accumulation of other metals in the copper-based alloy, containing more than 96 wt. % of the basic element, has been demonstrated by electric crucible melting in a highly reducing atmosphere. Copper-based alloys, after adjustment for the content of some metals (tin), can be realized as pressure-treated tin bronzes. Copper with the content of impurities corresponding to the standard for blister copper can be electrolytically processed (after dissolution in sulphuric acid) in copper production. Equipment for the implementation of the electro-thermal processing process that provides metal recycling of the metal concentrate is proposed.

The process experts are concerned in tellurium due to its various physical and chemical properties. The copper anode slime is the main industrial source of tellurium, after processing of that tellurium becomes marketable product and can be sold both in elemental form and tellurium-containing middling. Physical and chemical properties of the tellurium-containing middling of Kazakhmys Smelting LLP produced in 2018 have been studied in this paper. The following methods have been applied during the study: particle size distribution, X-ray phase, X-ray fluorescence and scanning electron probe microscopy. It was found that material is mainly represented by the large pieces of 0.2 mm in size, with moisture content of 15.57 %, bulk density of 0.8 g/cm3 without tapping and 0.88 g/cm3 with tapping, the angle friction - 33°. The elemental composition of the material was determined by X-ray fluorescence method as follows, wt. %: Cu – 33.327; Te – 21.863; Se – 0.766, O – 35.116; S – 5.045. X-ray phase analysis showed that material is mainly in the amorphous state, the following phases had been identified: Cu2.5SO4(OH)3·2H2O, Cu3(SO4)(OH)4, CuSO4(H2O)3. Tellurium-containing phases could not be detected due to strong amorphism. Hydrosulfate forms of copper in the form of flakes have been found on the surface of the middlings by electron probe microscopy. EDS analysis of individual areas showed that patina also contains small amounts of chlorine, selenium and up to 25 % tellurium, in addition to such elements as copper, sulfur and oxygen. Small amounts of sulfur, chromium, selenium and up to 45 % of oxygen has been found in the open area of material, that is specific for its oxidation.

This paper presents the results of a study of phase transformations occurring in copper-telluride by-products during its processing of oxidation-distillate roasting at low pressure. The results show that copper telluride is oxidized through intermediate compounds to the most stable tellurate (Cu₃TeO₆) at low temperatures. The increase in the roasting temperature above 900 °C and the presence of an oxidizer favor the copper orthotellurate decomposition. Thus, the tellurium extraction rate is 90–93% at a temperature of 1000 °C, the oxidant flow rate is 2.2 × 10⁻² m³/m²·s, and the roasting time is 60–90 min. One of the decomposition products is copper oxide alloy, which is the basis of the residue. The second product is tellurium in oxide form, which evaporates and then condenses in the cold zone of the condenser in crystalline form. The main constituent phase of the condensate is tellurium oxide (TeO₂), which can be further processed during one operation to elemental chalcogen by thermal reduction or electrolytic method.