A technology for the formation of electrically conductive nanostructures from single-walled carbon nanotubes (SWCNT), multi-walled carbon nanotubes (MWCNT), and their hybrids with reduced graphene oxide (rGO) on Si substrate has been developed. Under the action of single pulses of laser irradiation, nanowelding of SWCNT and MWCNT nanotubes with graphene sheets was obtained. Dependences of electromagnetic wave absorption by films of short and long nanotubes with subnanometer and nanometer diameters on wavelength are calculated. It was determined from dependences that absorption maxima of various types of nanotubes are in the wavelength region of about 266 nm. It was found that contact between nanotube and graphene was formed in time up to 400 fs. Formation of networks of SWCNT/MWCNT and their hybrids with rGO at threshold energy densities of 0.3/0.5 J/cm² is shown. With an increase in energy density above the threshold value, formation of amorphous carbon nanoinclusions on the surface of nanotubes was demonstrated. For all films, except the MWCNT film, an increase in defectiveness after laser irradiation was obtained, which is associated with appearance of C–C bonds with neighboring nanotubes or graphene sheets. CNTs played the role of bridges connecting graphene sheets. Laser-synthesized hybrid nanostructures demonstrated the highest hardness compared to pure nanotubes. Maximum hardness (52.7 GPa) was obtained for MWCNT/rGO topology. Regularity of an increase in electrical conductivity of nanostructures after laser irradiation has been established for films made of all nanomaterials. Hybrid structures of nanotubes and graphene sheets have the highest electrical conductivity compared to networks of pure nanotubes. Maximum electrical conductivity was obtained for MWCNT/rGO hybrid structure (~22.6 kS/m). Networks of nanotubes and CNT/rGO hybrids can be used to form strong electrically conductive interconnections in nanoelectronics, as well as to create components for flexible electronics and bioelectronics, including intelligent wearable devices (IWDs).

A technology for the formation and bonding with a substrate of hybrid carbon nanostructures from single-walled carbon nanotubes (SWCNT) and reduced graphene oxide (rGO) by laser radiation is proposed. Molecular dynamics modeling by the real-time time-dependent density functional tight-binding (TD-DFTB) method made it possible to reveal the mechanism of field emission centers formation in carbon nanostructures layers. Laser radiation stimulates the formation of graphene-nanotube covalent contacts and also induces a dipole moment of hybrid nanostructures, which ensures their orientation along the force lines of the radiation field. The main mechanical and emission characteristics of the formed hybrid nanostructures were determined. By Raman spectroscopy, the effect of laser radiation energy on the defectiveness of all types of layers formed from nanostructures was determined. Laser exposure increased the hardness of all samples more than twice. Maximum hardness was obtained for hybrid nanostructure with a buffer layer (bl) of rGO and the main layer of SWCNT—rGO(bl)-SWCNT and was 54.4 GPa. In addition, the adhesion of rGO to the substrate and electron transport between the substrate and rGO(bl)-SWCNT increased. The rGO(bl)-SWCNT cathode with an area of ~1 mm² showed a field emission current density of 562 mA/cm² and stability for 9 h at a current of 1 mA. The developed technology for the formation of hybrid nanostructures can be used both to create high-performance and stable field emission cathodes and in other applications where nanomaterials coating with good adhesion, strength, and electrical conductivity is required.

The present study aimed to improve the optical sensing performance of tapered optical fiber sensors toward aqueous Rhodamine B solution of different concentrations by applying single-walled carbon nanotubes (SWCNTs). The functional coating was formed on the surface of the tapered optical fiber sensor using an aerosol layer-by-layer deposition method. Before deposition, the SWCNTs were processed with multistage liquid-phase treatment in order to form a stable dispersion. The effect of SWCNT treatment was investigated through Raman spectroscopy. The deposition of 220 layers caused a reduction of up to 60% of the initial optical power of radiation propagating through the optical fiber core. The optical fiber sensor coated with SWCNTs demonstrated significantly higher sensitivity compared to a non-coated sensor in the range of 2–32 mg/L of Rhodamine B concentration in an aqueous solution. The experimental results demonstrated that the sensitivity was increased 10 times from 32 (mg/L)⁻¹, for the non-coated sensor, up to 317 (mg/L)⁻¹ after SWCNT coating deposition. Moreover, the SWCNT-coated sensor demonstrated high repeatability that allowed for the evaluation of the concentration regardless of the previously analyzed dye concentration.

Multilayer Al-CuO thermite materials are a prominent representative of metastable intermolecular composites, which are characterized by outstanding energy and combustion properties. In this work, we investigated the effect of the total thickness of the multilayer Al-CuO thermite material (enriched with aluminum), formed on the surface of sitall substrates, on the combustion mode and the morphology of the reaction products. High-speed video recording from different angles allowed us not only to estimate the combustion front propagation velocity, but also to visually estimate the gas evolution intensity. Using scanning electron microscopy in combination with a focused ion beam and energy-dispersive X-ray spectroscopy, the morphology and composition of the combustion products of the multilayer structures were studied. The obtained experimental data allowed us to describe three combustion modes of multilayer thermite materials in terms of the combustion front temperature and to relate this parameter to the total thickness of the multilayer structure.