Every year the problem of water purification becomes more relevant. This is due to the continuous increase in the level of pollution of natural water sources, an increase in the population, and sharp climatic changes. The growth in demand for affordable and clean water is not always comparable to the supply that exists in the water treatment market. In addition, the amount of water pollution increases with the increase in production capacity, the purification of which cannot be fully handled by conventional processes. However, the application of novel nanomaterials will enhance the characteristics of water treatment processes which are one of the most important technological problems. In this review, we considered the application of carbon nanomaterials in membrane water purification. Carbon nanofibers, carbon nanotubes, graphite, graphene oxide, and activated carbon were analyzed as promising materials for membranes. The problems associated with the application of carbon nanomaterials in membrane processes and ways to solve them were discussed. Their efficiency, properties, and characteristics as a modifier for membranes were analyzed. The potential directions, opportunities and challenges for application of various carbon nanomaterials were suggested.

Highly porous expanded graphite was synthesized by the programmable heating technique using heating with a constant rate (20 °C/min) from room temperature to 400–700 °C. The samples obtained were analyzed by scanning electron microscopy, energy-dispersive spectroscopy, low-temperature nitrogen adsorption, X-ray photoelectron spectroscopy, Raman spectroscopy, thermogravimetry, and differential scanning calorimetry. A comparison between programmable heating and thermal shock as methods of producing expanded graphite showed efficiency of the first one at a temperature 400 °C, and the surface area reached 699 and 184 m²/g, respectively. The proposed technique made it possible to obtain a relatively higher yield of expanded graphite (78–90%) from intercalated graphite. The experiments showed the advantages of programmable heating in terms of its flexibility and the possibility to manage the textural properties, yield, disorder degree, and bulk density of expanded graphite.