In this article, a facile way for the doping of graphene and graphene derivatives with silver nanoparticles at different Ag ratios is described. Ag nanoparticles were formed directly on the surface of two different graphene substrates dispersed in dimethylformamide by the reduction of Ag cations with NaBH₄. A few layered graphene nanosheets (FLG) produced from graphite and reduced graphene oxide functionalized with amino arylsulfonates (f-rGO) were used as substrates. The final graphene/Ag nanoparticle hybrid in the form of solid, dense spots showed enhanced electrical conductivity, which can be attributed to the formation of conductive interconnections between the 2D nanosheets. Importantly, electrical conductivities of 20 and 167 10³ S m⁻¹ were measured for the hybrids of f-rGO and FLG, respectively, with the higher Ag percentage without an annealing process. A representative hybrid f-rGO with Ag nanoparticles was used for the development of a highly conductive water-based gravure ink with excellent printing properties.

In this work, UV-curable resin poly (ethylene glycol) diacrylate (PEGDA) was reinforced with three different types of nanofillers: pristine graphene (G), multiwalled carbon nanotubes (MWNTs), and a hybrid of MWNTs and graphene 70/30 in mass ratio (Hyb). PEGDA was mixed homogenously with the nanofiller oligomer by shear mixing and then photopolymerized, affording thin, stable films. The thermomechanical properties of the afforded nanocomposites indicated the superior reinforcing ability of pristine graphene compared with MWNTs and an intermediate behavior of the hybrid.