An auxetic conductive cardiac patch (AuxCP) for the treatment of myocardial infarction (MI) is introduced. The auxetic design gives the patch a negative Poisson's ratio, providing it with the ability to conform to the demanding mechanics of the heart. The conductivity allows the patch to interface with electroresponsive tissues such as the heart. Excimer laser microablation is used to micropattern a re‐entrant honeycomb (bow‐tie) design into a chitosan‐polyaniline composite. It is shown that the bow‐tie design can produce patches with a wide range in mechanical strength and anisotropy, which can be tuned to match native heart tissue. Further, the auxetic patches are conductive and cytocompatible with murine neonatal cardiomyocytes in vitro. Ex vivo studies demonstrate that the auxetic patches have no detrimental effect on the electrophysiology of both healthy and MI rat hearts and conform better to native heart movements than unpatterned patches of the same material. Finally, the AuxCP applied in a rat MI model results in no detrimental effect on cardiac function and negligible fibrotic response after two weeks in vivo. This approach represents a versatile and robust platform for cardiac biomaterial design and could therefore lead to a promising treatment for MI.

Over the past few decades, significant progress has been made in the field of photonic processing of electronic materials using a variety of light sources. Several of these technologies have now been exploited in conjunction with emerging electronic materials as alternatives to conventional high‐temperature thermal annealing, offering rapid manufacturing times and compatibility with temperature‐sensitive substrate materials among other potential advantages. Herein, recent advances in photonic processing paradigms of metal‐oxide thin‐film transistors (TFTs) are presented with particular emphasis on the use of various light source technologies for the photochemical and thermochemical conversion of precursor materials or postdeposition treatment of metal oxides and their application in thin‐film electronics. The pros and cons of the different technologies are discussed in light of recent developments and prospective research in the field of modern large‐area electronics is highlighted.

High quality transparent conductive oxides (TCOs) often require a high thermal budget fabrication process. In this study, Excimer Laser Annealing (ELA) at a wavelength of 248nm has been explored as a processing mechanism to facilitate low thermal budget fabrication of high quality aluminium doped zinc oxide (AZO) thin films. 180nm thick AZO films were prepared by radio frequency magnetron sputtering at room temperature on fused silica substrates. The effects of the applied RF power and the sputtering pressure on the outcome of ELA at different laser energy densities and number of pulses have been investigated. AZO films deposited with no intentional heating at 180W, and at 2mTorr of 0.2% oxygen in argon were selected as the optimum as-deposited films in this work, with a resistivity of 1×10−3Ω.cm, and an average visible transmission of 85%. ELA was found to result in noticeably reduced resistivity of 5×10−4 Ω.cm, and enhancing the average visible transmission to 90% when AZO is processed with 5 pulses at 125mJ/cm2. Therefore, the combination of RF magnetron sputtering and ELA, both low thermal budget and scalable techniques, can provide a viable fabrication route of high quality AZO films for use as transparent electrodes

Peak temperature of a Ag thin film on Si and SEM images of the resultant nanoparticles by our MONA-LISA process.

Nonlinear metasurfaces have experienced rapid growth recently due to their potential in various applications, including infrared imaging and spectroscopy. However, due to the low conversion efficiencies of metasurfaces, several strategies have been adopted to enhance their performances, including employing resonances at signal or nonlinear emission wavelengths. This strategy results in a narrow operational band of the nonlinear metasurfaces, which has bottlenecked many applications, including nonlinear holography, image encoding, and nonlinear metalenses. Here, we overcome this issue by introducing a new nonlinear imaging platform utilizing a pump beam to enhance signal conversion through four-wave mixing (FWM), whereby the metasurface is resonant at the pump wavelength rather than the signal or nonlinear emissions. As a result, we demonstrate broadband nonlinear imaging for arbitrary objects using metasurfaces. A silicon disk-on-slab metasurface is introduced with an excitable guided-mode resonance at the pump wavelength. This enabled direct conversion of a broad IR image ranging from >1000 to 4000 nm into visible. Importantly, adopting FWM substantially reduces the dependence on high-power signal inputs or resonant features at the signal beam of nonlinear imaging by utilizing the quadratic relationship between the pump beam intensity and the signal conversion efficiency. Our results, therefore, unlock the potential for broadband infrared imaging capabilities with metasurfaces, making a promising advancement for next-generation all-optical infrared imaging techniques with chip-scale photonic devices.