The nanomaterials have been widely used in various fields, such as photonics, catalysis, and adsorption, because of their unique physical and chemical properties. Therefore, their production methods are of utmost importance. Compared with traditional synthetic methods, the template method can effectively control the morphology, particle size, and structure during the preparation of nanomaterials, which is an effective method for their synthesis. The key for the template method is to choose different templates, which are divided into hard template and soft template according to their different structures. In this paper, the effects of different types of templates on the morphology of nanomaterials during their preparation are investigated from two aspects: hard template and soft template, combined with the mechanism of action.

Carbon anodes play an important role in the electrolytic production of aluminum. They have a significant economic and environmental impact. Carbon anodes are made of dry aggregates, composed of petroleum coke, recycled rejects, and butts, bound by coal tar pitch. Due to several factors, defects (cracks/pores) appear in anodes during the fabrication process, affecting their quality. It is thus essential to control the quality of anodes before their use in the electrolysis cell. Current practice for the quality evaluation (visual inspection, core analysis) gives limited information. As an alternative to this practice, electrical resistivity measurements can be used. Electrical resistivity is one of the key indicators for anode quality and its homogeneity. A simple and non-destructive method has been developed for the specific electrical resistivity measurement of anodes (SERMA) for on-line control of anode quality. Various tests have been carried out at both lab scale and industrial scale. In this study, the electrical resistivity distributions in the lab-scale anodes were measured and compared with those of the tomography analysis. The method is able to detect defective anodes even before the baking process.

In order to reduce greenhouse gas (GHG) emissions, biocoke modified with different additives was used to replace part of the petroleum coke. Previously, a number of researchers attempted to manufacture anodes using biocoke. However, the majority of these efforts were unsuccessful because the quality of the anodes deteriorated with this replacement. The deterioration was due to the weak interactions between the pitch and biocoke compared to those between the pitch and petroleum coke. In this study, a chemical modification of biocoke was carried out using three additives (i.e., A(1), A(2), and A(3)) with the aim of improving biocoke–pitch interactions to prevent the deterioration of anode quality. The results of this study showed that biocoke–pitch interactions improved when the biocoke was modified with A(1) and A(3). The anodes containing biocoke modified with these two additives had properties similar to those of the standard anode (i.e., without biocoke). The utilization of additive A(2) did not show the same trend.