Actually, in order to replace traditional fossil-based polymers, many efforts are devoted to the design and development of new and high-performance bioplastics materials. Poly(hydroxy alkanoates) (PHA_S) as well as polylactides are the main candidates as naturally derived polymers. The intention of the present study is to manufacture fully bio-based blends based on two polyesters: poly (3-hydroxybutyrate) (PHB) and polylactic acid (PLA) as real competitors that could be used to replace petrol polymers in packaging industry. Blends in the shape of films have been prepared by chloroform solvent cast solution methodology, at different PHB/PLA ratios: 1/0, 1/9, 3/7, 5/5, 0/1. A series of dynamic explorations have been performed in order to characterize them from a different point of view. Gas permeability to N₂, O₂, and CO₂ gases and probe (TEMPO) electron spin resonance (ESR) analyses were performed. Blend surface morphology has been evaluated by Scanning Electron Microscopy (SEM) while their thermal behavior was analyzed by Differential Scanning Calorimetry (DSC) technique. Special attention was devoted to color and transparency estimation. Both probe rotation mobility and N₂, O₂, and CO₂ permeation have monotonically decreased during the transition from PLA to PHB, for all contents of bio-blends, namely because of transferring from PLA with lower crystallinity to PHB with a higher one. Consequently, the role of the crystallinity was elucidated. The temperature dependences for CO₂ permeability and diffusivity as well as for probe correlation time allowed the authors to evaluate the activation energy of both processes. The values of gas transport energy activation and TEMPO rotation mobility are substantially close to each other, which should testify that polymer segmental mobility determines the gas permeability modality.

Non-woven polylactide-natural rubber fiber materials with a rubber content of 5, 10 and 15 wt.% were obtained by electrospinning. The thermal, dynamic, and mechanical properties of the fibers were determined. It was shown that the average fiber diameter increased with adding of the NR content, while the linear and surface densities changed slightly. Using the differential scanning calorimetry, the thermal characteristics were obtained. It was found that the glass transition temperature of polylactide increased by 2–5 °C, and the melting temperature increased by 2–4 °C in the presence of natural rubber in the samples. By the method of electronic paramagnetic resonance at T = 50 and 70 °C it was determined that the mobility of the amorphous phase in PLA/NR fibers increased with the addition of NR. The adding of NR at a content of 15 wt.% increased the value of elongation at break by 3.5 times compared to pure PLA.

In this work, PLA/NR electrospun fibers were used as substrates for growing basil. Thermal characteristics of initial samples and after 60 and 220 days of degradation were determined using differential scanning calorimetry. In the process of disintegration, the melting and glass transition temperatures in PLA/NR composites decreased, and in PLA fibers these values increased slightly. TGA analysis in an argon environment confirmed the effect of NR on the thermal degradation of PLA/NR fibers. After exposure to the soil for 220 days, the beginning of degradation shifted to the low-temperature region. The dynamic characteristics of the fibers were determined by the EPR method. A decrease in the correlation time of the probe-radical in comparison with the initial samples was shown. FTIR spectroscopy was used to analyze the chemical structure before and after degradation in soil. In PLA/NR fibrous substrates, there was a decrease in the intensity of the bands corresponding to the PLA matrix and the appearance of N-H C-N groups due to biodegradation by soil microorganisms.

The effect of small amounts of the zinc–tetraphenylporpyrin complex (1–5%) on the structure and properties of ultrathin fibers based on poly(3-hydroxybutyrate) is investigated using...

The effect of small additions of the iron(III) complex with tetraphenylporphyrin (0–5%) on the structure and properties of ultrathin fibers based on poly(3-hydroxybutyrate) (PHB) was studied by...