Natural fibers do not have a long life in soil; therefore, they cannot replace synthetic textiles in many applications. However, in order to solve ever-increasing global environmental problems due to microplastics, more and more natural polymers must be used, creating a need for research into the sustainable life extension of natural fibers. Lignin is, along with cellulose, a main component of wood, and is produced in large quantities as waste during paper production. With appropriate processing, lignin can be exploited/used as a textile auxiliary to combine the strength-enhancing properties of textiles made from natural fibers with the protective properties of a lignin coating. However, there is not yet sufficient research on how to integrate lignin into textile applications. For this purpose, in this study, we have investigated whether thermoplastic lignin can be processed as a surface protective coating. We tested lignin as a yarn coating to extend the service life of cellulosic textiles. Cotton yarns have been coated with lignin in variations of coating mass, characterized and investigated by means of soil burial tests. As the soil burial tests conducted in climate chamber and outdoor field environments showed, the lifespan of textiles made from natural fibers can be significantly extended with a lignin coating. Long-term resilience has been demonstrated in standard burial tests. In the outdoor tests, the lignin coating was still fully intact, even after about 160 days of burial. The textile materials coated in this way enable sustainable applications, especially for geotextiles. They have an adjustable, sufficiently long service life; however, they are still biodegradable, and can therefore replace some applications, such as vegetating trench/brook slopes, with synthetic materials. Lignin-coated textiles have the potential to significantly reduce the carbon footprint, reduce not only the dependence on petroleum-based products but also the amount of microplastics entering the environment. Further research can be conducted to improve lignin compounding in terms of other interesting properties for specific textile applications. Process optimization could increase the protective effect and further extend the life of useful textiles in soil.

The present experimental work analyses the potential of lignin as a matrix for materials made from renewable resources for composite components and the production of hybrid semi-finished products by coating a flax fibre yarn. Natural fibres, due to their low density, in combination with lignin can be a new renewable source for lightweight products. For this purpose, the extrusion process was adapted to lignin as a matrix material for bio-based composites and coating of natural fibre yarns. A commercial flax yarn is the basis for the lignin coating by extrusion. Subsequently, the coated flax yarn was characterised with regard to selected yarn properties. In order to produce composite plates, the lignin-coated flax yarn was used as warp yarn in a bidirectional fabric due to its insufficient flexibility transversely to the yarn axis. The commercial flax yarn was used as weft yarn to increase the fibre volume content. The tensile and flexural properties of the bio-based composite material were determined. There was a significant difference in the mechanical properties between the warp and weft directions. The results show that lignin can be used as matrix material for bio-based natural fibre composites and the coating of natural fibre yarns is an alternative to spun hybrid yarns.

Betel nut is one of the important fruits cultivated in tropical parts of the world. It generates a huge quantity of husk, which is a source of areca fiber. Both fine and coarse fibers are available in the husk. Different properties of fine areca fiber have been analyzed for qualifying its ability to convert into spun yarn. Fine areca fiber has good physical properties in terms of length, water absorption, maturity which makes it suitable for spinning. However, in case of strength and fineness it showed ordinary value compared to cotton fiber. Areca/cotton 50:50 blend 48 tex ring and rotor yarn has been produced and yarns showed tenacity 7.1cN/tex and 6.88 cN/tex accompanied by 6.81% and 6.35% elongation, respectively. The water absorption of areca/cotton blend yarn showed 4.8 times higher value than 100% cotton yarn.

This study presents the development of a textile-based cascade filter for the removal of microplastics from an industrial laundry effluent. The cascade microfilter consists of three stages of 3D textile sandwich composite filter media, which have successively finer pores and are aimed at filtering microplastic particles down to 1.5 µm. Polypropylene fabrics with pore sizes of 100, 50 and 20 µm and 3D warp-knitted fabrics with high porosity (96%) were used. Filtration tests were carried out with polyethylene model microplastic particles at a concentration of 167 mg/L. To regenerate the filter and restore its filtration performance, backwashing with filtered water and compressed air was applied. Field trials at an industrial laundry facility and a municipal wastewater treatment plant confirmed high removal efficiencies. The 3D textile sandwich structure promotes filter cake formation, allowing extended backwash intervals and the effective recovery of filtration capacity between 89.7% and 98.5%. The innovative use of 3D textile composites enables a high level of microplastic removal while extending the filter media lifetime. This makes a significant contribution to the reduction in microplastic emissions in the aquatic environment. The system is scalable, space and cost efficient and adaptable to various industrial applications and is thus a promising solution for advanced wastewater treatment.