Increasing resource consumption and a growing amount of textile waste increase the importance of a circular economy and recycling in the fashion and apparel industry. Environmentally friendly bio-based composites made from cellulosic fibres obtained from textile waste, and polymers based on renewable raw materials present a possible solution. In this study, the development of textile semi-finished products based on medium-to-long cotton and flax fibres obtained from textile waste in combination with a bio-based thermoplastic matrix for lightweight applications is investigated. For the production of natural fibre-polylactide hybrid yarns, fibre slivers with improved fibre orientation and blending are produced. Subsequently, quasi-unidirectional woven fabrics are produced and consolidated into bio-based composites. Textile and mechanical properties of hybrid yarns as well as bio-composites are analysed with regard to the influence of fibre length, fibre distribution in the yarn, yarn structure and fibre volume content. The results show that the production of bio-based semi-finished products can be a potential way for upcycling textile waste.

In order to sustainably establish carbon fiber reinforced polymer composites (CFRPC) in the market on an industry scale, solutions on how to recycle these new materials have to be developed. Quasi-continuously aligned carbon staple fiber structures in organic sheets made of recycled carbon are one approach which will be dealt with in this article. The process chain as well as the mechanical properties will be presented. Moreover, the specific feature of staple fiber yarns to be able to plastically deform under process temperature, enabling new degrees of deep-drawing of CFRPC organic sheets in the thermoforming process, will be highlighted.

Although fiber-reinforced plastics combine high strength and stiffness with being lightweight, major difficulties arise with high volume production and the return of manufactured parts back into the cycle of materials at the end of their lifecycles. In a novel approach, structural parts were produced from recycled material while utilizing the so-called injection molding compounding process. Recycled fibers and recycled polyamide matrix material were used by blending carbon and matrix fibers into a sliver before processing. Injection molding was then used to produce long fiber-reinforced parts through a direct fiber feed system. Recycled matrix granules were incorporated into the injection molding process by means of an injection molding compounder to investigate their influences on the mechanical properties of the parts. The findings show that the recycled fibers and matrix perform well in standardized tests, although fiber length and fiber content vary significantly and remain below expectations.

Increasing waste streams of carbon fibers (CF) and carbon fiber reinforced plastics (CFRP) lead to increasing need for recycling and to growing amounts of recycled carbon fibers. A main issue in current research for carbon fiber recycling is the reuse of regained fibers. Carbon staple fibers such as recycled fibers hold big potential for mechanical properties of lightweight parts, if used properly. Applying recycled CF (rCF) as milled reinforcement fibers or as nonwoven in carbon fiber reinforced plastic leads to a poor yield of mechanical proper due to low fiber orientation, limitations in fiber volume content or due to short fiber length. The rC staple fiber tape presents a more efficient approach. Recycled carbon fibers are blended with 50 wt. % thermoplastic nylon 6 fibers and processed through a roller card to a sliver, which is a linear fibrous intermediate. The sliver is continuously drawn, formed, heated and consolidated to the thermoplastic rC staple fiber tape. The tape is similar to common carbon fiber tapes or to continuous tows but has different positive properties, such as high fiber orientation, homogeneous blend of fiber and matrix and suitability for deep drawing.

The aim of this study was to characterise the microstructural organisation of staple carbon fibre-reinforced polymer composites and to investigate their mechanical properties. Conventionally, fibre-reinforced materials are manufactured using continuous fibres. However, discontinuous fibres are crucial for developing sustainable structural second-life applications. Specifically, aligning staple fibres into yarn or tape-like structures enables similar usage to continuous fibre-based products. Understanding the effects of fibre orientation, fibre length, and compaction on mechanical performance can facilitate the fibres’ use as standard engineering materials. This study employed methods ranging from microscale to macroscale, such as image analysis, X-ray computed tomography, and mechanical testing, to quantify the microstructural organisations resulting from different alignment processing methods. These results were compared with the results of mechanical tests to validate and comprehend the relationship between fibre alignment and strength. The results show a significant influence of alignment on fibre orientation distribution, fibre volume fraction, tortuosity, and mechanical properties. Furthermore, different characteristics of the staple fibre tapes were identified and attributed to kinematic effects during movement of the sliver alignment unit, resulting in varying tape thicknesses and fuzzy surfaces.

The present experimental work analyses the potential of lignin as a matrix for materials made from renewable resources for composite components and the production of hybrid semi-finished products by coating a flax fibre yarn. Natural fibres, due to their low density, in combination with lignin can be a new renewable source for lightweight products. For this purpose, the extrusion process was adapted to lignin as a matrix material for bio-based composites and coating of natural fibre yarns. A commercial flax yarn is the basis for the lignin coating by extrusion. Subsequently, the coated flax yarn was characterised with regard to selected yarn properties. In order to produce composite plates, the lignin-coated flax yarn was used as warp yarn in a bidirectional fabric due to its insufficient flexibility transversely to the yarn axis. The commercial flax yarn was used as weft yarn to increase the fibre volume content. The tensile and flexural properties of the bio-based composite material were determined. There was a significant difference in the mechanical properties between the warp and weft directions. The results show that lignin can be used as matrix material for bio-based natural fibre composites and the coating of natural fibre yarns is an alternative to spun hybrid yarns.