Introducing lignocellulosic fibers as the matrix reinforcement in composites is an opportunity for weight reduction and also for the use of by-products and biomass waste from other systems, such as agriculture and textiles. In the case of nautical applications, biofouling, meaning damage during service by marine organisms, represents a significant issue. To address this problem, a number of measures can be taken: these include the introduction of various types of fillers, mainly mineral, in composites, tailored treatment of fibers, and hybrid approaches, including a number of different modifications, such as matrix or fiber grafting. This review reports the state of the art in the various studies carried out to elucidate the performance of natural fiber composites and hybrids as regards water absorption and more specifically exposure to seawater for a prolonged time so as to simulate service conditions. The perspectives on the use of natural fiber composites (NFCs) in aquatic environments will be discussed with respect to the possible onset of degradation by biofouling.

The analysis of cruise ships is focusing on port areas where they may represent a significant source of anthropogenic emissions. In order to determine the correlation between cruise ship activities (hoteling and maneuvering) in ports with the ambient concentration of pollutants associated with marine diesel fuel combustion, the low-cost sensors are finding their market share due to lower prices compared to the referent ones. In this study, a network of four low-cost PM sensors was used to determine the correlation between ambient PM_2.5 and PM₁₀ mass concentrations with cruise ship activities in the Kotor Bay area during 27 days in the peak summer season, with a 10-min resolution. Recorded data and the Openair model were used to investigate the potential relationship between cruise ship operations and temporal fluctuations in PM concentrations in the ambient air. Additionally, an Tier 3 methodology developed through the European Monitoring and Evaluation Programme of the European Environmental Agency (EMEP/EEA) was applied in order to estimate the total cruise ship PM emissions. The study has shown that weather conditions play a significant role in local PM concentrations, so that, with predominant ENE wind directions, the west side of the Bay experienced on average higher concentrations of both PM_2.5 and PM₁₀. Rain precipitation and higher winds tend to decrease rapidly ambient PM concentrations. Higher PM levels are associated mainly with lower wind speeds and the inflows from neighboring berths/anchorages. During the maneuvering (arrival and departure) of cruise ships, higher spikes in PM values were detected, being more visible for PM₁₀ than PM_2.5. A significant correlation between daily average PM concentrations and cruise ships’ daily estimated PM emission was not found. As a result, higher temporal resolution demonstrated a stronger correlation.

This research explores the potential introduction of marine waste-derived biological fillers within bio-epoxy matrices to mitigate the environmental impact of traditional materials, like fiberglass, in boat construction. However, this raises concerns about biofouling and degradation, issues that have not been extensively investigated in composites, especially over a time frame representative of issues that could arise during service. Although protective solutions like biocides and specific coatings exist, degradation remains challenging when attempting to use eco-friendly natural fillers. This study specifically integrates various biological fillers, namely ceramics (mussel, oyster, clam powder) or ligno-cellulosic (i.e., Posidonia oceanica fibers) into epoxy for use in some boat components (bench seats for the bridge deck), aiming to evaluate the biofouling process under extreme (or decommissioning) conditions. In itself, epoxy does represent an ideal enclosing matrix for biomass waste, which ideally needs to be introduced in significant amounts. The development of biofouling in the specific context of Kotor’s Bay, Montenegro, for a duration of six months, and relevant composite degradation were examined. In particular, three situations were reproduced by positioning the samples in a harbor environment: (i) on the bottom of the sea (2 m. depth), (ii) immersed just below the surface (0.5 m. depth), and (iii) on the splashing surface (pier). The concerns identified appear generally limited in the case of the envisaged application, despite some significant wear effect in the case of the samples containing Posidonia. However, this study also offers information and caveats in terms of more ambitious prospective applications (e.g., the boat hull structure).