Supplementary cementitious material (SCM) plays an important role in blended cement, and the effect of the particle size and morphology of siliceous supplementary cementitious material on hydration should not be ignored. In this study, 0.5 h and 1 h of wet grinding was applied to pretreat iron ore tailing powder (TP), and the divergence in pozzolanic behavior and morphology were investigated. Then, the treated TPs were used to replace the 30% cement contents in preparing blended cementitious paste, and the impact mechanism of morphology on performance was studied emphatically. M, the autogenous shrinkages of pastes were tested. Finally, hydration reaction kinetics was carried out to explore the hydration behavior, while X-ray diffraction (XRD) and thermogravimetric analysis (TGA) were used to characterize the hydration product properties, respectively. Meanwhile, microscopy intrusion porosimetry (MIP) was also carried out to characterize the pore structures of hardened specimens. Results indicated that wet grinding has a dramatic effect on particle size and morphology, but hardly affects the phase assemblages and pozzolanic reactivity of TP, while the particle shape of TP changes from sub-circular to clavate and, finally, back to sub-circular. The results of hydration reaction kinetics, representing the morphology of particles, had a significant effect on hydration rate and total heat, and compared with the sub-circle one, the clavated particle could inhibit the hydration procedure. With the increasing grinding time, the compressive strength of cementitious paste was increased from 17.37% to 55.73%, and the micro-pore structure became denser; however, the autogenous shrinkage increased.

In this study, a type of fly ash and iron tailing powder were used as a binary supplementary cementitious material (SCM) and two different mechanically activated procedures, named coalescent activation and separated activation, were carried out to improve the pozzolanic reactivity. Then, three binary supplementary cementitious materials were used to replace 30 wt% of ordinary Portland cement to develop cemented mortars, and the compressive strength, hydration products, and micro-structure were studied. The experimental results indicated that the activated supplementary cementitious materials increased the compressive strengths of the mortars by 5.4% and 13.2%, negligibly changed the hydration product types, and impacted the quantity only. The application of SCMs also prolonged the setting time and decreased the hydration rate, profiting the application. Simultaneously, the micro-pore structure was ameliorated, and the porosity decreased. Therefore, comprehensively considering the improved mechanical behavior and inexpensive cost, the activated binary SCM can be considered an ecological and economical admixture, especially for the coalescent activation procedure.

Utilizing a variety of solid wastes to prepare alkali-activated cementitious materials is one of the principal trends in the development of cementitious materials. Commonly used alkali activation precursors such as granulated blast furnace slag (GBFS) and fly ash (FA) will be less available due to resource pressures. Supply limitation is an important reason to research alternative precursors. To realize the high value-added utilization of copper–molybdenum tailings (CMTs), this study adopted the modified sodium silicate solution as an alkaline activator to activate GBFS-FA-CMTs cementitious system to prepare alkali-activated cementitious materials. The influence of CMTs content on the compressive strength of GBFS-FA-CMTs cementitious system was analyzed, and the mechanism of GBFS-FA-CMTs cementitious system was also analyzed through hydration product types, physical phase composition, and microscopic morphology. The results indicated that a paste with the incorporation of CMTs, S50F30C20 (50% GBFS, 30% FA, 20% CMTs), achieved the highest compressive strength of 79.14 MPa, which was due to the filling effect of the CMTs and the degree of participation in the reaction. Pastes with different contents of CMTs, while maintaining a constant CBFS content, exhibited similar strength development. Excessive amounts of CMTs could result in reduced compressive strength. Microstructural analysis revealed that the hydration products were structurally altered by the addition of CMTs. In addition to ettringite, quartz, C(-N)-S-H gel, and calcite, gaylussite was also formed; moreover, the mass of chemically bound water increased, and the microstructure of reaction products became denser. An excess of CMTs may restrict the growth of the hydration gel, leading to more microstructural defects. The study suggests that CMTs could enhance the compressive strength of hardened paste within an alkali-activated slag-fly ash system, possibly due to a filling effect and participation in the chemical reaction. This research confirms the feasibility of using CMTs in alkali-activated cementitious materials.