This study investigated the effects of plasma duration and different reactive species ratios of cold atmospheric-pressure plasma treatment on both physical and endogenous hormone changes in enhancing the germination and growth of mung bean seeds. Seed germination and sprout stem length were significantly enhanced after plasma treatment. The germination rate increased eleven times after 12 h, while the radicles’ length increased ~3 times after 96 h with optimal plasma treatment parameters. SEM images showed that the plasmas directly induced gradual changes in the seed coating, including deformed and shrunken epidermis, and cracks with sizes varying from 0.2 to 1.5 µm after 4 min of plasma treatment. Water contact angle was reduced from 73° with untreated seed to almost 0° with 4 min treated seed. These effects could lead to better water absorption on the surface of treated seeds. We found that a plasma energy dosage of 0.08 Wh per seed and NO concentration between 20–95 ppm were the optimal enhancement conditions. We also showed that, for the first time, through delicate extraction, separation, and quantification processes, NO-induced upregulation of the natural growth hormone gibberellic acid could be the dominant phytochemistry pathway responsible for the enhancement effect.

In this paper, we report a simple yet efficient method for rapid and high-performance SERS substrate fabrication by a combination of cold plasma and laser treatment. Our analysis reveals that cold plasma pre-treatment significantly reduced surface roughness, transforming 200 nm spikes into an almost perfectly uniform surface, while enhancing the substrate’s surface energy by lowering the water contact angle from 59° to 0°, all achieved within just 30 s of 0.9-mW plasma treatment, while 15-min green-laser treatment facilitated more uniform deposition of AuNPs across the entire treated area, effectively creating the SERS substrates. The combined treatments result in enhancement of the Raman intensity (11 times) and consistency over the whole area of the SERS substrates, and their reusability (up to 10 times). The fabricated SERS substrates exhibit a significant enhancement factor of approximately 3 × 10⁸ with R6G, allowing detection down to a concentration of 10⁻¹² M. We demonstrate the application of these SERS substrates by detecting amoxicillin—an antibiotic used worldwide to treat a diversity of bacterial infections—in a dynamic expanded linear range of seven orders (from 10⁻³ to 10⁻⁹ M) with high reliability (R² = 0.98), and a detection limit of 9 × 10⁻¹⁰ M. Our approach to high-performance SERS substrate fabrication holds potential for further expansion to other metallic NPs like Ag, or magnetic NPs (Fe₃O₄).