This article reviews lithium recovery methods from primary resources and lithium raw materials processing methods. Lithium world reserves as well as deposits by countries are given. Summary of global market for and marketing of lithium raw materials are provided. The main lithium recovery methods from minerals (sulphate, lime, sulphuric) are shown. The data about obtaining in Kazakhstan an experimental sample of lithium carbonate from spodumene ore is provided.

In order to obtain sulfur-containing organophosphorus compounds that are promising as extractants of heavy metals, the interaction of elemental phosphorus and sulfur with alkyl bromides catalyzed using strong bases was studied. According to the task, the reaction of non-toxic and non-flammable red phosphorus with alkyl bromides under conditions of phase transfer catalysts (PTC), followed by the introduction of elemental sulfur into the reaction medium, were studied. It is shown that alkyl bromides interact with red phosphorus when heated (95–105 °C, 5–8 h) under conditions of phase transfer catalysts (PTC) in a two-phase system: a 60% aqueous solution of KOH-toluene-benzyltriethylammonium chloride (BTEAC) forming a mixture of organophosphorus compounds along with alkylphosphines (57–60%), are the main reaction products; alkylphosphine oxides are also formed (40–43%). The introduction of elemental sulfur (solution in toluene) at the final stage of the process into the reaction mass cooled to 40–60 °C leads to the expected alkylphosphine sulfides, which are the result of the interaction of alkylphosphines with sulfur. The formation of complex mixtures of products prevents the release of target alkylphosphine sulfides in individual form. However, the synthesized mixture of alkylphosphine sulfides and alkylphosphine oxides without separation into individual components is promising for studying its extraction properties in relation to heavy metals. Testing of the extraction properties of synthesized mixtures of alkylphosphine sulfides and alkylphosphine oxides in relation to heavy metals (Ni, Co, Zn, Pb) and noble metals (Ag) showed that the resulting mixtures of tertiary phosphine oxides and phosphine sulfides are highly effective extractants. The degree of extraction in relation to Ni, Co, Zn, and Pb varies from 99.90 to 99.99%, and for Ag from 99.56 to 99.59%.

By kinetics, volumetry, gas chromatography, elemental analysis, IR, NMR spectroscopy the oxidative alkoxylation of yellow phosphorus to phosphorus esters in alcohol solutions of copper and iron salts...

Today, lithium is becoming a new strategic material capable of influencing the sustainable development of the world economy. The results of developments in the production of innovative electrode materials from lithium carbonate on the basis of domestic lithium-containing raw materials with the creation of a full cycle of the technological line of lithium production: from ores to modern lithium batteries are pesented. Analysis of the explored reserves, mineral and material composition of domestic spodumene raw materials and lithium-containing dumps of the Belogorsk GOK indicate the prospects and expediency of their development for the production of the ever-increasing needs of the world market for lithium materials. As a result, the sulfuric acid technology for obtaining high-grade lithium carbonate directly from spodumene was optimized, bypassing the stage of obtaining a technical grade product, in a single technological process for processing spodumene with a reduction in the number of technological operations, excluding the expensive operation of concentrating a lithium sulfate solution by stripping. An efficient technology of purification and post-treatment of technical lithium carbonate to battery quality of 99.95% has been developed, including the processes of causticization of technical lithium carbonate, ultrafiltration and ion-exchange sorption of a solution of lithium hydroxide, followed by precipitation of lithium carbonate by ammonium carbonate. Cathode materials - lithium iron-phosphate , obtained from high-purity lithium carbonate by aerosol pyrolysis (MAP) and the sol-gel method (SGM), showed good electrochemical characteristics. The end result is innovative electrode materials for modern LIBs with significantly increased capacity and stability. The practical implementation of a full cycle of technologies from lithium-containing raw materials to modern lithium batteries opens up prospects for the creation in Kazakhstan of a high-tech lithium cluster according to the Scheme: Spodumene ores → Lithium concentrate → Lithium carbonate → Lithium cathode materials → Batteries.

Bis-N,N-(3-triethoxysilylpropyl)thiosemicarbazide 3 was obtained by the condensation of 3-aminopropyltriethoxysilane 1 with thiosemicarbazide 2. Ethyl ether N-[3-(triethoxysilyl)propyl]-b-alanine 5 was obtained by the interaction of an equimolar amount of aminopropyltriethoxysilane 1 and ethyl acrylate 4 (aza-Michael reaction). Synthesized functional organosilanes 3 and 5 were successfully immobilized on the surface of natural zeolite Z (Chankanai deposit, Kazakhstan). Compounds and materials have been studied by NMR and IR Fourier spectroscopy and X-ray diffraction analysis. The elemental composition and morphology of modified zeolites Z3 and Z5 were studied using SEM-EDX analysis. The modification of zeolite by organosilanes 3 and 5 leads to changes in the surface structure of the material: with the enlargement of particles and agglomerates, the surface becomes more homogeneous and less porous. This indicates a high degree of zeolite coverage by the modifier layer. The study of the sorption characteristics of the initial Z and modified zeolites (Z3 and Z5) showed a high sorption capacity relative to Ag(I) and Co(II) (static sorption capacity, SSC = 35.85–23.92 mg/g), whereas the SSC values for Z were SSC = 20.63 and 16.64 mg/g. The adsorption of Ag(I) and Co(II) ions was studied in solutions prepared using Co(NO₃)₂·6H₂O, AgNO₃ and distilled water. The choice of the initial concentration of metal ions, as well as the pH of the solutions, corresponded to the composition of wastewater from real electroplating production. Zeolites Z3 and Z5 can be used in various sectors of industry, in ecology and for medical purposes as inexpensive and effective adsorbents (enterosorbents) of heavy and noble metals.