Chemical components with anti-oxidant, anti-inflammatory, and anti-cancer properties extracted from Alnus bark and leaves have been extensively studied. However, less attention has been paid to extractives from Alnus pods, which are mostly treated as waste. Here, extractives of Alnus cremastogyne pods from 12 provenances in Sichuan Province were studied for high value-added utilization of Alnus waste. The extractives were analyzed by Gas Chromatography-Mass Spectrometer (GC-MS), Ultraviolet-visible spectroscopy (UV-Vis spectra), and 1,1-diphenyl-2-picrylhydrazyl (DPPH) scavenging activity. A total of 58, 49, and 51 chemical components were found when the organic solvents of ethanol, petroleum ether, and ethyl acetate were used to collect extractives, respectively. These chemical components including Phytol, CIS-5,8,11,14,17-eicosapentaenoic acid, Germacrene D, Lupeol, and β-sitosterol, etc., have wide applications in the fields of pharmacy and cosmetics. Moreover, it was also found that extractives in ethanol and ethyl acetate had impressive UV resistance, especially for UV-C and UV-B blocking. The results showed that the maximum block ratio towards UV-C and UV-B could reach 99%. In addition, the ethanol extract showed good anti-oxidant activity with a maximum free radical scavenging rate of 96.19%. This comprehensive and systematic study on extractives from Alnus cremastogyne pods promotes the development of high-value utilization of Alnus components.

Photocatalytic oxidation is considered one of the most effective ways to remove formaldehyde from indoor air. However, the use of powder photocatalysts is limited by their low adsorption capacity and strong aggregation tendency. Hence, there is a need for a composite material with good cycling stability and high degradation efficiency. In the present study, a unique wood-based composite is produced by arranging Cu–TiO₂ nanoparticles on porous structured wood. The porous structure of wood can adsorb formaldehyde, and the abundant functional groups on the surface can act as a reaction platform for anchoring the Cu–TiO₂ nanoparticles. Cu doping facilitates electron interaction between TiO₂ and Cu, promotes the transfer of charge carriers, lowers the electron–hole recombination rate, and improves the photocatalytic degradation efficiency of formaldehyde. The photocatalytic efficiency of the wood-based composites was highest (85.59%) when the n(Cu)/n(Ti) ratio was 7%. After nine cycles, the wood composites still had a high degradation rate, indicating good recyclability. Overall, this wood composite is an eco-friendly and promising material for indoor air filtration.