Particle boards are manufactured through a hot pressing process using wood materials (natural polymer materials) and adhesive, which find common usage in indoor decorative finishing materials. Flame-retardant particleboard, crucial for fire safety in such applications, undergoes performance analysis that includes assessing temperature distribution across its facing surface and temperature increase on the backside surface during facade combustion, yielding critical insights into fire scenario development. In this study, a compact flame spread apparatus is utilized to examine the flame retardancy and combustion behavior of particle boards, with a specific emphasis on the application of cost-effective flame retardants, encompassing aluminum hypophosphite (ALHP), an intumescent flame retardant (IFR) comprising ammonium polyphosphate (APP), melamine (MEL), and Dipentaerythritol (DPE), alongside magnesium hydroxide (MDH), and their associated combustion characteristics. The D_300°C values, representing the vertical distance from the ignition point (IP) to P_300°C (the temperature point at 300 °C farthest from IP), are measured using a compact temperature distribution measurement platform. For MDH/PB, APP + MEL + DPE/PB, and ALHP/PB samples, the respective D_300°C values of 145.79 mm, 117.81 mm, and 118.57 mm indicate reductions of 11.11%, 28.17%, and 27.71%, compared to the untreated sample’s value of 164.02 mm. The particle boards treated with ALHP, IFR, and MDH demonstrated distinct flame-retardant mechanisms. MDH/PB relied on the thermal decomposition of MDH to produce MgO and H₂O for flame retardancy, while APP + MEL + DPE/PB achieved flame retardancy through a cross-linked structure with char expansion, polyphosphate, and pyrophosphate during combustion. On the other hand, ALHP/PB attained flame retardancy by reacting with wood materials and adhesives, forming a stable condensed P-N-C structure. This study serves as a performance reference for the production of cost-effective flame-resistant particleboards and offers a practical method for assessing its fire-resistant properties when used as a decorative finishing material on facades in real fire situations.

In this work, ethyl acetate (EA) and trichloromethane (TR) extracts were extracted from Phoebe zhennan wood residues and the extracts were then applied to the preparation of UV shielding films (UV-SF). The results revealed that substances including olefins, phenols and alcohols were found in both EA and TR extracts, accounting for about 45% of all the detected substances. The two extracts had similar thermal stability and both had strong UV shielding ability. When the relative percentage of the extract is 1 wt% in solution, the extract solution almost blocked 100% of the UV-B (280–315 nm), and UV-A (315–400 nm). Two kinds of UV-SF were successfully prepared by adding the two extracts into polylactic acid (PLA) matrix. The UV-SF with the addition of 24 wt% of the extractive blocked 100% of the UV-B (280–315 nm) and more than 80% of the UV-A (315–400 nm). Moreover, the UV shielding performance of the UV-SF was still stable even after strong UV irradiation. Though the addition of extracts could somewhat decrease the thermal stability of the film, its effect on the end-use of the film was ignorable. EA extracts had less effect on the tensile properties of the films than TR extracts as the content of the extract reached 18%. The results of this study could provide fundamental information on the potential utilization of the extracts from Phoebe zhennan wood residues on the preparation of biobased UV shielding materials.

Chemical components with anti-oxidant, anti-inflammatory, and anti-cancer properties extracted from Alnus bark and leaves have been extensively studied. However, less attention has been paid to extractives from Alnus pods, which are mostly treated as waste. Here, extractives of Alnus cremastogyne pods from 12 provenances in Sichuan Province were studied for high value-added utilization of Alnus waste. The extractives were analyzed by Gas Chromatography-Mass Spectrometer (GC-MS), Ultraviolet-visible spectroscopy (UV-Vis spectra), and 1,1-diphenyl-2-picrylhydrazyl (DPPH) scavenging activity. A total of 58, 49, and 51 chemical components were found when the organic solvents of ethanol, petroleum ether, and ethyl acetate were used to collect extractives, respectively. These chemical components including Phytol, CIS-5,8,11,14,17-eicosapentaenoic acid, Germacrene D, Lupeol, and β-sitosterol, etc., have wide applications in the fields of pharmacy and cosmetics. Moreover, it was also found that extractives in ethanol and ethyl acetate had impressive UV resistance, especially for UV-C and UV-B blocking. The results showed that the maximum block ratio towards UV-C and UV-B could reach 99%. In addition, the ethanol extract showed good anti-oxidant activity with a maximum free radical scavenging rate of 96.19%. This comprehensive and systematic study on extractives from Alnus cremastogyne pods promotes the development of high-value utilization of Alnus components.