Carbon nanowall (CNW) and carbon nanotube (CNT) were prepared as anode materials of lithium-ion batteries. To fabricate a lithium-ion battery, copper (Cu) foil was cleaned using an ultrasonic cleaner in a solvent such as trichloroethylene (TCE) and used as a substrate. CNW and CNT were synthesized on Cu foil using plasma-enhanced chemical vapor deposition (PECVD) and water dispersion, respectively. CNW and CNT were used as anode materials for the lithium-ion battery, while lithium hexafluorophosphate (LiPF₆) was used as an electrolyte to fabricate another lithium-ion battery. For the structural analysis of CNW and CNT, field emission scanning electron microscope (FE-SEM) and Raman spectroscopy analysis were performed. The Raman analysis showed that the carbon nanotube in composite material can compensate for the defects of the carbon nanowall. Cyclic voltammetry (CV) was employed for the electrochemical properties of lithium-ion batteries, fabricated by CNW and CNT, respectively. The specific capacity of CNW and CNT were calculated as 62.4 mAh/g and 49.54 mAh/g. The composite material with CNW and CNT having a specific capacity measured at 64.94 mAh/g, delivered the optimal performance.

In this paper, a new synthesis of carbon nanofibers (CNFs)/carbon nanowalls (CNWs) was performed to improve the characteristics of anode materials of lithium-ion batteries by using the advantages offered by CNWs and CNFs. Among the carbon-based nanomaterials, CNWs provide low resistance and high specific surface area. CNFs have the advantage of being stretchable and durable. The CNWs were grown using a microwave plasma-enhanced chemical vapor deposition (PECVD) system with a mixture of methane (CH₄) and hydrogen (H₂) gases. Polyacrylonitrile (PAN) and N,N-Dimethyl Formamide (DMF) were stirred to prepare a solution and then nanofibers were fabricated using an electrospinning method. Heat treatment in air was then performed using a hot plate for stabilization. In addition, heat treatment was performed at 800 °C for 2 h using rapid thermal annealing (RTA) to produce CNFs. A field emission scanning electron microscope (FE-SEM) was used to confirm surface and cross-sectional images of the CNFs/CNWs anode materials. Raman spectroscopy was used to examine structural characteristics and defects. Cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and constant current charge/discharge tests were performed to analyze the electrical characteristics. The synthesized CNFs/CNWs anode material had a CV value in which oxidation and reduction reactions were easily performed, and a low Rct value of 93 Ω was confirmed.

Carbon, which exists in large quantities on Earth, is a material with interesting properties, and many studies have been conducted since the past. In particular, nano-sized carbon allotropes are called carbon nanomaterials, and many studies are currently underway. Among them, carbon nanowall (CNW) is a structure in which graphene of sp2 bond is grown vertically, CNW have outstanding strength, can be highly electrically conducting or semiconducting, have a large specific surface area per unit mass. Electrical, chemical, physical properties of these CNW is modified by parameter such as surface density, height and thickness of it. Those have great effect on CNW and can be adjusted as growth interlayer. It was confirmed that the molybdenum disulfide (MoS2) interlayer synthesized by radio frequency (RF) magnetron sputtering altered the morphological characteristics such as the shaped edge of the CNW, the pores diameter and density. Through these studies, we confirmed the effect of MoS2 on the morphological characteristics of CNW. This opens the door to improving the performance of electrodes and devices.

Carbon is a material with interesting properties which exists in large quantities on Earth, so many studies involving carbon have been conducted. In particular, nano-sized carbon allotropes, referred to as carbon nanomaterials, comprise the subject of various studies currently underway. The electrical, chemical, physical properties of carbon nanowalls (CNWs) are modified by parameters such as surface density, height and thickness. These characteristics have significant effects on CNWs and can be adjusted as a growth interlayer. It was confirmed that the molybdenum disulfide (MoS₂) interlayer synthesized in this paper by radio frequency (RF) magnetron sputtering altered the morphological characteristics of the CNWs, including its shaped edge, pores diameter and density. We provide interesting results through FE-SEM, EDS and Raman analysis in this paper. Based on the Raman analysis, both the D-peak of carbon and the I_D/I_G ratio decreased. Through this study, the effect of MoS₂ on the morphological characteristics of CNWs was confirmed.