This study aimed to use quantitative and qualitative evaluations based on micro-tensile bond strength (μTBS) to clarify the appropriate immediate dentin sealing (IDS) approach for improving the bonding of CAD/CAM ceramic crown restorations. Forty-eight extracted human molars were prepared to obtain standardized abutment specimens and divided into three groups: no IDS (group C: control), IDS performed by a single application of an all-in-one adhesive system (group A), and IDS performed by the combined application of an adhesive system and a flowable resin composite (group F). All specimens were restored with a ceramic crown fabricated by a chair-side CAD/CAM system and were divided into no-stress and stressed groups. After cyclic loading (78.5 N; total, 3 × 105 cycles; 90 cycles/min) on the specimens in the stressed group, all specimens were sectioned. The μTBS values for the occlusal and mesioaxial walls were measured (n = 16) and analyzed statistically. The quantitative bonding performance of groups A and F were superior to that of group C, regardless of the cyclic loading and abutment wall conditions. Group F showed the maximum bond strength and the highest bond durability in the qualitative bonding performance even under the cyclic loading condition simulating clinical mastication.

Incremental techniques are always required for clinical cases of deep and/or large cavities restored with resin composite materials. The purpose of this study was to examine the bonding states of class 2 direct resin composite restoration applied by various incremental techniques after cyclic loading to simulate the intra-oral environment to define the appropriate technique. Three types of resin composites, namely, bulk-fill (B), flowable (F), and conventional resin composite (C), were applied to standardized class 2 cavities by incremental techniques with single- or bi-resin restoratives. After cyclic loading, the micro-tensile bond strength (μ-TBS) of the dentin cavity floor was measured. The Weibull modulus and Weibull stress values at 10%/90% probability of failure were analyzed. Single-resin incremental restorations with B or F and bi-resin incremental restorations with F + B and F + C demonstrated superior μ-TBS (quantitative ability), bonding reliability, and durability (qualitative ability) compared with the single-resin restoration with C (as control). Furthermore, F + B and F + C restoration yielded an excellent performance compared with the single-resin restorations with B, F, and C. In particular, the F + C restoration, which indicates not only the maximum mean µ-TBS, but also the highest values of the Weibull parameters, may be the optimal restoration method, including the esthetic benefits.

This study evaluated the effect of simulated pulpal pressure (SPP) conditions and storage time on contemporary adhesive systems’ microtensile bond strength (µTBS) to dentin. Extracted human molars were prepared and randomly divided into four groups according to the adhesives: Clearfil Megabond 2 (CSE), Beautibond Xtreme Universal (BXU), G2-Bond (G2B), and Scotchbond Universal Plus (SBP). Each adhesive group was further divided following the SPP conditions: control with no simulation (SPP-CTR), SPP with distilled water (SPP-DTW), and SPP with fetal bovine serum (SPP-FBS). Resin composite build-ups were prepared, and teeth were stored in water (37 °C) for 24 h (24 h) and 3 months (3 m). Then, teeth were sectioned to obtain resin–dentin bonded beams and tested to determine the µTBS. Data were analyzed using three-way ANOVA, Tukey post hoc tests (=0.05), and Weibull failure analysis. Failure mode was observed using scanning electron microscopy. The µTBS response was affected by adhesive systems, simulated pulpal pressure conditions, and storage time. SPP-CTR groups presented a higher overall bond strength than SPP-DTW and SPP-FBS, which were not significantly different from each other. Only for SBP, the SPP-FBS group showed higher µTBS than the SPP-DTW group. The Weibull analysis showed that the bonding reliability and durability under SPP-DTW and SPP-FBS were inferior to SPP-CTR, and the 24 h bonding quality of adhesives to dentin was superior to that of 3 m. SPP drastically reduced the µTBS of all adhesives to dentin regardless of solution (distilled water or fetal bovine serum). Storage after 3 m also decreased µTBS despite the SPP condition.