The purpose of this study was to evaluate the microtensile bond strength (µTBS) and Knoop hardness number (KHN) of a novel experimental light-cured resin cement (HL). Eighteen flat dentin surfaces of human molars were polished using #600 SiC paper and bonded to CAD/CAM resin blocks with the respective resin cements and composites: HL, Panavia V5 (PV), and Clearfil AP-X (AP). All specimens were stored in distilled water at 37 °C for 24 h and 7 days. Scanning electron microscope (SEM) and energy dispersive X-ray (EDX) observations were performed to evaluate filler morphology and to detect the elements. The resin cements had a significant effect on the immediate µTBS (F = 22.59, p < 0.05) and after water storage µTBS (F = 22.83, p < 0.05). Significant differences (p < 0.05) in the KHN between the tested materials were observed, and HL indicated the highest KHN when compared with PV. HL showed a combination of the regular-shaped filler and spherical-shaped filler within the matrix. Silicon was detected in HL from the EDX evaluation. HL exhibited better bonding performance and polymerization, which may have contributed to the improvement of the adhesive strength.

This study evaluated the effect of a 0.5% chloramine T solution on a chemical-cured universal adhesive by comparing the light-cured, one-step, self-etch adhesive for the bonding performance, mechanical properties, and resin–dentin interfacial characteristics. Caries-free human molars were randomly assigned into eight groups based on the bonding systems employed (Bond Force II, BF and Bondmer Lightless, BL), the immersion solutions used before bonding (0.5% chloramine T solution and distilled water), and the immersion durations (5 and 60 min). Microtensile bond strength (μTBS), nanoleakage evaluation, and nanoindentation tests were performed, and the surface morphology of the resin–dentin interface was examined using a focus ion beam/scanning ion microscopy system. Immersion in chloramine-T for 5 min significantly decreased the μTBS of Bondmer Lightless (from 22.62 to 12.87 MPa) compared with that in distilled water. Moreover, there was also a decreasing trend after immersing in chloramine-T for 60 min (from 19.11 to 13.93 MPa). Chloramine T was found to have no effect on the hardness, elastic modulus, or morphological characteristics of the ion-beam milled resin–dentin interfacial surfaces in the tested adhesives, suggesting that chloramine T might reduce the bond strength by interfering with the interaction and the sealing between the adhesive resin and dentin in the chemical-cured universal adhesive, albeit without affecting the mechanical properties.

This study evaluated the effect of simulated pulpal pressure (SPP) conditions and storage time on contemporary adhesive systems’ microtensile bond strength (µTBS) to dentin. Extracted human molars were prepared and randomly divided into four groups according to the adhesives: Clearfil Megabond 2 (CSE), Beautibond Xtreme Universal (BXU), G2-Bond (G2B), and Scotchbond Universal Plus (SBP). Each adhesive group was further divided following the SPP conditions: control with no simulation (SPP-CTR), SPP with distilled water (SPP-DTW), and SPP with fetal bovine serum (SPP-FBS). Resin composite build-ups were prepared, and teeth were stored in water (37 °C) for 24 h (24 h) and 3 months (3 m). Then, teeth were sectioned to obtain resin–dentin bonded beams and tested to determine the µTBS. Data were analyzed using three-way ANOVA, Tukey post hoc tests (=0.05), and Weibull failure analysis. Failure mode was observed using scanning electron microscopy. The µTBS response was affected by adhesive systems, simulated pulpal pressure conditions, and storage time. SPP-CTR groups presented a higher overall bond strength than SPP-DTW and SPP-FBS, which were not significantly different from each other. Only for SBP, the SPP-FBS group showed higher µTBS than the SPP-DTW group. The Weibull analysis showed that the bonding reliability and durability under SPP-DTW and SPP-FBS were inferior to SPP-CTR, and the 24 h bonding quality of adhesives to dentin was superior to that of 3 m. SPP drastically reduced the µTBS of all adhesives to dentin regardless of solution (distilled water or fetal bovine serum). Storage after 3 m also decreased µTBS despite the SPP condition.