In situ composite manufacture is an approach to improve interfacial adhesion between matrix and reinforcements, in which reinforcements are synthesized along composite processing itself. In situ powder metallurgy route, in particular, offers alternatives to some shortcomings found in other techniques. This work aims not only to review the state of the art on metal matrix composites (MMCs)—including cermets—obtained in situ by powder metallurgy, but also to dissect key aspects related to the development of such materials in order to establish theoretical criteria for decision making before and along experiments. Aspects regarding the design, raw material selection, and processing of such composites were observed and divided between concept, intrinsic, and extrinsic parameters. That way, by means of material databases and computational thermodynamics applied to examples of the reviewed literature, we aim at providing tools in both conducting leaner experiments and richer discussion in this field.

The development of beta titanium alloys with biocompatible elements to replace Al and V is a subject of significant interest in the biomedical industry. This approach aims to enhance biocompatibility and mitigate potential cytotoxic effects associated with traditional alloying elements. In this work, Ti–xNb–ySi alloys were produced using powder metallurgy, with x of 35, 40, and 45 wt.%, and y of 0.10, 0.35, and 0.60% wt.%, using a $3^2$ experimental design. Milling was used to mix and disperse the powders, followed by cold pressing, sintering, and heat treatment. Nb was the main element used to stabilize the β phase, and Si was used to form Si precipitates, although Si also exhibits a β-stabilizing effect. It was found that an increase from 0.10 to 0.35 wt.% of Si improved relative density, with no benefits observed at 0.60 wt.% Si. Electron microscopy showed the presence of β phase grains, and grains with β + α intragranular structures and precipitates. Increasing Nb content resulted in a decrease in ultimate tensile strength while increasing Si content from 0.10% to 0.35 wt.% exhibited the opposite effect.