A polysaccharide was extracted in high yield from tamarind (Tamarindus indica L.) seed (TSP) by acidic hot water extraction and ethanol precipitation. It was composed of 86.2% neutral polysaccharide, 5.4% uronic acid and 1.3% protein. The molecular weight of TSP was estimated to be about 1735 kDa, with glucose, xylose, and galactose in a molar ratio of 2.9:1.8:1.0 as the major monosaccharides. The steady shear and viscoelastic properties of TSP aqueous solutions were investigated by dynamic rheometry. Results revealed that TSP aqueous solution at a concentration above 0.5% (w/v) exhibited non-Newtonian shear-thinning behavior. Dynamic oscillatory analysis revealed that 10% (w/v) TSP showed as a “weak gel” structure. Apparent viscosities and viscoelastic parameters of TSP solutions decreased drastically in an alkaline solution of pH > 10, but slightly influenced by acidic solution, high temperature and the presence of salt ions and sucrose. These results indicated that TSP possessed excellent pH-resistance and thermo-stability, which might be suitable for applications in acidic beverages and high-temperature processed foodstuffs.

The synergistic interaction and gelling kinetics between xanthan gum (XG) and locust bean gum (LBG) at different mass ratios (XG/LBG 9:1, 7:3, 5:5, 3:7, 1:9) were investigated using a rheometer. The results showed that the mixtures of XG and LBG induced gel formation, and the strongest gel structure was found for the mixture of XG/LBG 3:7 according to the yield stress, storage modulus (G′), and power law parameters. Temperature ramp studies indicated that heating destroyed the gels at 55~60 °C, while cooling induced the sol–gel transition at around 52 °C for all mixtures. Structure developing rate (SDR) curves showed that XG/LBG 3:7 exhibited the highest SDR during the cooling ramp among all the samples. Non-isothermal kinetic analysis demonstrated that the gelation process of XG/LBG mixtures during cooling included two steps: a high-temperature region (55~39 °C) needing higher activation energy (Ea, 111.97 to 199.20 kJ/mol for different mixtures) and a low-temperature region (39~20 °C) needing lower Ea (74.33 to 85.31 kJ/mol), which indicated higher energy barriers to overcome at the initial stage of gel formation. The lowest Ea of 74.33 kJ/mol was found for XG/LBG 3:7 in the low-temperature region. Scanning electron microscopy (SEM) showed that the gel of XG/LBG 3:7 presented the densest entanglements. These results indicated the strongest synergism interaction occurred in XG/LBG 3:7 to form gel network structures. This study will help promote the application of XG-LBG blends to design novel food structures.