Localized surface plasmon (LSP) coupling with many radiators are investigated. The LSP is generated by excitation of laser or electron beam on the random Ag nano particles (NPs) and arrayed ones embedded in the p-GaN of green LEDs. They couple with the excitons or radiative recombination in the quantum well (QW) and electron beam, which enhance or suppress the luminescence of the radiators. The photoluminescence (PL) intensity of periodic Ag NPs can get as much as 4.5 times higher than that of bare LED. In addition to the periodic structure, the morphology of Ag NPs also affects the localized SP (LSP) resonance intensity and light scattering efficiency. In the finite difference time domain (FDTD) simulation, five x-polarized dipoles are approximated to five quantum wells. Considering the interaction between the five dipoles and their feedback effect on LSP, the enhancement effect of SP dipole coupling with Ag NPs is amplified and the energy dissipation is reduced. The enhancement of cathodoluminescence (CL) was also found in green LEDs with Ag NPs. The three-body model composed of two orthogonal dipoles and an Ag NP is used for 3D FDTD simulation. The LSP-QWs coupling effect is separated from the electron beam (e-beam)-LSP-QW system by linear approximation. Under the excitation of electron beam, the introduction of z-dipole greatly reduces the energy dissipation. In the cross-sectional sample, z-polarized dipoles in QWs show more coupling strength to the dipole and quadrupole modes of LSP. The perturbation theory is used to separate the LSP coupling effects to x-dipole and z-dipole. At last, the resonator and the antenna effects are discussed for LSP coupling at different positions to the Ag NP.

Nanorod array and planar green-emission InGaN/GaN multi-quantum well (MQW) LEDs were fabricated by lithography, nano-imprinting, and top–down etching technology. The defect-pinning effect of the nanostructure was found for the first time. The ratio of the bright regions to the global area in the panchromatic CL images of green MQW samples increased from 30% to about 90% after nano-fabrication. The overall luminous performance significantly improved. Throughout temperature-dependent photoluminescence (TDPL) and time-resolved PL (TRPL) measurements, the migration and recombination of carriers in the MQWs of green LEDs were analyzed. It was proved that nanostructures can effectively prevent carriers from being captured by surrounding nonradiative recombination centers. The overall PL integral intensity can be enhanced to above 18 times. A much lower carrier lifetime (decreasing from 91.4 to 40.2 ns) and a higher internal quantum efficiency (IQE) (increasing from 16.9% to 40.7%) were achieved. Some disputes on the defect influence were also discussed and clarified.

Different morphology of ZnO were deposited on GaN substrate using magnetron sputtering method by changing deposition conditions. The ZnO and GaN can form II-type heterojunction due to its higher conduction and lower valence band compared to GaN. The electric field generated by space charge region can separate the photo generated carriers more promptly. In the photocatalytic test, the best performance of GaN/ZnO photoanode with fine crystal quality is about 1.39 times compared to planar GaN. Our research paves a new way for the application of GaN in water splitting performance.