Ablation of copper using multipulse femtosecond laser irradiation with an 800 nm wavelength and 120-fs pulse duration is investigated theoretically. A two-temperature model, which includes dynamic optical and thermal-physical properties, is considered. The numerical results of the material thermal response obtained by varying the pulse number, the separation times between pulses and laser fluences are presented. Our results show that the increasing of pulse number with a separation time less than the thermal relaxation time can dramatically enhance the lattice temperature without a noticeable increase in ablation depth. Therefore, we suggest that the vaporization rate can be augmented in comparison to the melting rate during the same single-phase explosion at the same total fluence where a fast heat accumulation effect plays an important role for cleaner ablation during micromachining.

In this study, we theoretically investigate the response of a germanium thin film under femtosecond pulsed laser irradiation. Electron and lattice temperatures, as well as material-specific optical properties such as dielectric function and reflectivity, were calculated during the irradiation using an extended two-temperature model coupled with the carrier density rate equation and the Drude model. Melting and ablation fluence thresholds were also predicted, resulting in 0.14 J cm⁻² and 0.35 J cm⁻², respectively. An ultrafast change in both optical and thermal properties was detected upon laser irradiation. Results also indicate that thermal melting occurs after germanium takes on a metallic character during irradiation, and that the impact ionization process may have a critical role in the laser-induced thermal effect. Therefore, we suggest that the origin of the thermal modification of germanium surface under femtosecond laser irradiation is mostly due the impact ionization process and that its effect becomes more important when increasing the laser fluence.