The environmental degradation of poly(ε-caprolactone)[PCL] in natural fresh water (pond) and in The Baltic Sea is presented in this paper. The characteristic parameters of both environments were measured during experiment and their influence on the biodegradation of the samples was discussed. The loss of weight and changes of surface morphology of polymer samples were tested during the period of incubation. The poly(ε-caprolactone) was more biodegradable in natural sea water than in pond. PCL samples were completely assimilated over the period of six weeks incubation in The Baltic Sea water, but after forty two weeks incubation in natural fresh water the polymer weight loss was about 39%. The results have confirmed that the investigated polymers are susceptible to an enzymatic attack of microorganisms, but their activity depends on environments.

This study aims to estimate the degradation process of polylactide (PLA) in natural aqueous environments. The biological degradation of PLA took place in the Baltic Sea and in the natural pond over a period of 1 to 16 months. The characteristic abiotic parameters of both environments were monitored during incubation time, and their influence on the PLA degradation was discussed. The changes in weight, chemical structure, mechanical properties and surface morphology of investigated samples were also tested during incubation. The obtained results indicate that polylactide is not very susceptible to an enzymatic attack of microorganisms present in natural aqueous environments.

Polyether-esterurethanes containing synthetic poly[(R,S)-3-hydroxybutyrate] (R,S-PHB) and polyoxytetramethylenediol in soft segments and polyesterurethanes with poly(ε-caprolactone) and poly[(R,S)-3-hydroxybutyrate] were blended with poly([D,L]-lactide) (PLA). The products were tested in terms of their oil and water absorption. Oil sorption tests of polyether-esterurethane revealed their higher response in comparison to polyesterurethanes. Blending of polyether-esterurethanes with PLA caused the increase of oil sorption. The highest water sorption was observed for blends of polyether-esterurethane, obtained with 10% of R,S-PHB in soft segments. The samples mass of polyurethanes and their blends were almost not changed after incubation in phosphate buffer and trypsin and lipase solutions. Nevertheless the molecular weight of polymers was significantly reduced after degradation. It was especially visible in case of incubation of samples in phosphate buffer what suggested the chemical hydrolysis of polymer chains. The changes of surface of polyurethanes and their blends, after incubation in both enzymatic solutions, indicated on enzymatic degradation, which had been started despite the lack of mass lost. Polyurethanes and their blends, contained more R,S-PHB in soft segments, were degraded faster.

E3S Web of Conferences, open access proceedings in environment, energy and earth sciences