Here, ultraviolet light-emitting diodes (UV-LED) combined with TiO₂ was used to investigate the feasibility of carbamazepine (CBZ) degradation. The effects of various factors, like crystal form of the catalyst (anatase, rutile, and mixed phase), mass concentration of TiO₂, wavelength and irradiation intensity of the UV-LED light source, pH of the reaction system, and coexisting anions and cations, on the photocatalytic degradation of CBZ were studied. The mixed-phase (2.8 g/L) showed the best degradation efficiency at 365 nm among three kinds of TiO₂, wherein CBZ (21.1 µM) was completely oxidized within 1 h. The results of batch experiments showed that: (i) CBZ degradation efficiency under UV-LED light at 365 nm was higher than 275 nm, due to stronger penetrability of 365 nm light in solution. (ii) The degradation efficiency increased with increase in irradiation intensity and pH, whereas it decreased with increase in initial CBZ concentration. (iii) The optimal amount of mixed-phase TiO₂ catalyst was 2.8 g/L and excessive catalyst decreased the rate. (iv) The co-existence of CO₃²⁻, HCO₃⁻, and Fe³⁺ ions in water significantly accelerated the degradation rate of photocatalytic CBZ, whereas Cu²⁺ ions strongly inhibited the degradation process of CBZ. ·OH was found to be the main active species in the UV-LED photocatalytic degradation of CBZ. UV-LED is more environmentally friendly, energy efficient, and safer, whereas commercial TiO₂ is economical and readily available. Therefore, this study provides a practically viable reference method for the degradation of pharmaceuticals and personal care products (PPCPs).

A novel malachite green molecularly imprinted membrane (MG-MIM) with specific selectivity for malachite green (MG) and leucomalachite green (LMG) was prepared using a hydrophobic glass fiber membrane as the polymer substrate, methyl violet as a template analog, 4-vinyl benzoic acid as the functional monomer, and ethyleneglycol dimethacrylate as the crosslinking agent. MG-MIM and non-imprinted membrane (NIM) were structurally characterized using scanning electron microscopy, surface area analyzer, Fourier-transform infrared spectrometer and synchronous thermal analyzer. The results showed that MG-MIM possessed a fluffier surface, porous and looser structure, and had good thermal stability. Adsorption properties of MG-MIM were investigated under optimal conditions, and adsorption equilibrium was reached in 20 min. The saturated adsorption capacities for MG and LMG were 24.25 ng·cm⁻² and 13.40 ng·cm⁻², and the maximum imprinting factors were 2.41 and 3.20, respectively. Issues such as “template leakage” and “embedding” were resolved. The specific recognition ability for the targets was good and the adsorption capacity was stable even after five cycles. The proposed method was successfully applied for the detection of MG and LMG in real samples, and it showed good linear correlation in the range of 0 to 10.0 μg·L⁻¹ (R² = 0.9991 and 0.9982), and high detection sensitivity (detection limits of MG and LMG of 0.005 μg/kg and 0.02 μg·kg⁻¹ in shrimp, and 0.005 μg/kg and 0.02 μg/kg in fish sample). The recoveries and relative standard deviations were in the range of 76.31–93.26% and 0.73–3.72%, respectively. The proposed method provides a simple, efficient and promising alternative for monitoring MG and LMG in aquatic products.

To evaluate the efficacy of biochelators for phytoremediation of cadmium (Cd), effects of biochelators (humic acid, HA; polyaspartic acid, PASP; rhamnolipid, RLs) and synthetic chelator (sodium tripolyphosphate, STPP) on the growth, accumulation, and antioxidant index of Cd were investigated in Iris sibirica L. The results indicated that the addition of HA increased the dry weight of leaves and stems, and the addition of PASP, RLs, and STPP increased the growth of leaves but inhibited the growth of stems. The determination of Cd accumulation indicated that HA decreased the content of Cd in all tissues, while the addition of PASP, RLs, and STPP increased the accumulation of Cd in stems and roots. In addition, the determination of superoxide dismutase (SOD), peroxidase (POD), and catalase (CAT) activities indicated that the treatment of PASP and RLs increased the activities of antioxidant enzymes, which might be beneficial to the resistance of Cd for Iris sibirica L. Overall, these results indicated that biochelators may improve the phytoremediation efficacy of Iris sibirica L. on Cd polluted paddy field. Among the tested chelators, PASP exhibited the best comprehensive efficacy and the highest commercial potential.

Polyvinylidene fluoride (PVDF) membranes are favored for their excellent properties. However, the inherent strong hydrophobicity of PVDF membranes limits their development in the field of water treatment. The objective of this study was to improve the performance of PVDF membranes using the self-polymerization, strong adhesion properties, and biocompatible effects of dopamine (DA). The PVDF/DA membrane modification conditions were simulated and optimized using response surface methodology (RSM), and the experimental design was used to investigate three main parameters. The results showed that the DA solution concentration of 1.65 g/L, the coating time of 4.5 h, the post-treatment temperature of 25°C, the contact angle decreased from 69° to 33.9°, and the pure water flux on the PVDF/DA membrane was higher than that on the original membrane. The absolute value of the relative error between the actual and predicted values is only 3.36 %. In the MBR parallel comparison test, compared with the PVDF/DA membrane, the total amount of extracellular polymers (EPS) of the PVDF membrane increased by 1.46 times and the polysaccharide increased by 1.56 times, which further showed that the PVDF/DA modified membrane had the excellent anti-pollution ability. Through Alpha diversity analysis, the biodiversity detected on PVDF/DA membranes was higher than that of PVDF membranes, which further proved its good bio-adhesion ability. These findings could offer a reference for the hydrophilicity, antifouling, and stability of PVDF/DA membranes, which would establish the foundation for the comprehensive applications in MBR.