The loss of mechanical properties affecting archeological or paleontological bones is often caused by demineralization processes that are similar to those driving the mechanisms leading to osteoporosis. One simple way to harden and to strengthen demineralized bone remains could be the in situ growth of CaCO₃ crystals in the aragonite polymorph – metastable at atmospheric pressure −which is known to have very strong mechanical strength in comparison with the stable calcite. In the present study the controlled growth of aragonite crystals was achieved by reaction between atmospheric CO₂ and calcium hydroxide nanoparticles in the presence of collagen within the deteriorated bones. In a few days the carbonation of Ca(OH)₂ particles led to a mixture of calcite and aragonite, increasing the strength of the mineral network of the bone. Scanning electron microscopy coupled with energy dispersive X-ray spectroscopy (SEM–EDS) and Fourier transform infrared (FT-IR) spectrometry showed that aragonite crystallization was achieved. The effect of the aragonite crystal formation on the mechanical properties of the deteriorated bones was investigated by means of X-rays microtomography, helium porosimetry, atomic force microscopy (AFM), and Vickers microhardness techniques. All these data enabled to conclude that the strength of the bones increased of a factor of 50–70% with respect to the untreated bone. These results could have immediate impact for preserving archeological and paleontological bone remains.

Copper alloy artworks are particularly subjected to chloride attack, which may trigger bronze disease. Therefore, early identification of the phenomenon is crucial in order to stabilize the reactive copper chloride (CuCl) and remove the harmful corrosion products (atacamite and polymorphs). Confocal Raman Microspectroscopy (CRM) has proven to be effective for the detection of small amounts of atacamite, ascribable to the initial phases of corrosion. The handling of bronze artworks is often difficult or even impossible given their large size and weight, and sampling is not always allowed, making the use of portable instruments mandatory for on-site diagnostics. This paper proposes a method for the early detection of corrosion using non-invasive approaches. In this work, we present the results obtained from a set of artificially aged bronze samples with a suite of either laboratory (bench-top) or field (portable/transportable) instruments with the aim of highlighting their characteristics and performances in the diagnosis of bronze disease. Raman spectroscopy, Fiber Optics Reflectance Spectroscopy (FORS), Optical Coherence Tomography (OCT), and Scanning Electron Microscopy (SEM) were applied for chemical and morphological characterization of the samples.

The combination of two different metals, each of them acting on different steps of the oxygen reduction reaction (ORR), yields synergic catalytic effects. In this respect, the electrocatalytic effect of silver is enhanced by the addition of cobalt, which is able to break the O–O bond of molecular oxygen, thus accelerating the first step of the reduction mechanism. At the same time, research is to further reduce the catalyst’s cost, reducing the amount of Ag, which, even though being much less expensive than Pt, is still a noble metal. From this point of view, using a small amount of Ag together with an inexpensive material, such as graphite, represents a good compromise. The aim of this work was to verify if the synergic effects are still operating when very small amounts of cobalt (2–10 μg·cm⁻²) are added to the microparticles of silver electrodeposited on glassy carbon, described in a preceding paper from us. To better stress the different behaviour observed when cobalt and silver are contemporarily present in the deposit, the catalytic properties of cobalt alone were investigated. The analysis was completed by the Levich plots to evaluate the number of electrons involved and by Tafel plots to show the effects on the reaction mechanism.