This study aims to model grinding of a Polish ferronickel slag and evaluate the particle size distributions (PSDs) of the products obtained after different grinding times. Then, selected products were alkali activated in order to investigate the effect of particle size on the compressive strength of the produced alkali activated materials (AAMs). Other parameters affecting alkali activation, i.e., temperature, curing, and ageing time were also examined. Among the different mathematical models used to simulate the particle size distribution, Rosin–Rammler (RR) was found to be the most suitable. When piecewise regression analysis was applied to experimental data it was found that the particle size distribution of the slag products exhibits multifractal character. In addition, grinding of slag exhibits non-first-order behavior and the reduction rate of each size is time dependent. The grinding rate and consequently the grinding efficiency increases when the particle size increases, but drops sharply near zero after prolonged grinding periods. Regarding alkali activation, it is deduced that among the parameters studied, particle size (and the respective specific surface area) of the raw slag product and curing temperature have the most noticeable impact on the compressive strength of the produced AAMs.

In this study, the alkali activation potential of a Polish ferronickel slag (PS), for the production of inorganic polymers (IPs), is investigated. The effect of the main synthesis parameters, i.e., strength of the activating solution, consisting of NaOH and Na₂SiO₃ solutions and affecting (SiO₂ + Al₂O₃)/Na₂O and other important molar ratios in the reactive paste, pre-curing period, curing temperature and time and ageing period was investigated. The structural integrity of the produced specimens was tested after their (i) immersion in distilled water and acidic solutions for a period of 7–30 days, and (ii) firing at temperatures between 200 °C and 1000 °C. Several analytical techniques including X-ray diffraction, X-ray fluorescence, Fourier transform infrared spectroscopy, Differential scanning analysis-Thermogravimetry and Scanning Electron Microscopy were used for the characterization of the produced IPs. Results show that under the optimum synthesis conditions the IPs obtain compressive strength that exceeds 65 MPa. An innovative aspect of this study is that after heating at 400 °C, the specimens acquire compressive strength of 115 MPa and this indicates that they can be also used as fire resistant materials. This study highlights the potential of alkali activation for the valorization of a ferronickel slag and the production of IPs that can be used as binders or in several construction applications, thus improving the sustainability of the metallurgical sector.