This study aims to model grinding of a Polish ferronickel slag and evaluate the particle size distributions (PSDs) of the products obtained after different grinding times. Then, selected products were alkali activated in order to investigate the effect of particle size on the compressive strength of the produced alkali activated materials (AAMs). Other parameters affecting alkali activation, i.e., temperature, curing, and ageing time were also examined. Among the different mathematical models used to simulate the particle size distribution, Rosin–Rammler (RR) was found to be the most suitable. When piecewise regression analysis was applied to experimental data it was found that the particle size distribution of the slag products exhibits multifractal character. In addition, grinding of slag exhibits non-first-order behavior and the reduction rate of each size is time dependent. The grinding rate and consequently the grinding efficiency increases when the particle size increases, but drops sharply near zero after prolonged grinding periods. Regarding alkali activation, it is deduced that among the parameters studied, particle size (and the respective specific surface area) of the raw slag product and curing temperature have the most noticeable impact on the compressive strength of the produced AAMs.

In this study, the alkali activation potential of a Polish ferronickel slag (PS), for the production of inorganic polymers (IPs), is investigated. The effect of the main synthesis parameters, i.e., strength of the activating solution, consisting of NaOH and Na₂SiO₃ solutions and affecting (SiO₂ + Al₂O₃)/Na₂O and other important molar ratios in the reactive paste, pre-curing period, curing temperature and time and ageing period was investigated. The structural integrity of the produced specimens was tested after their (i) immersion in distilled water and acidic solutions for a period of 7–30 days, and (ii) firing at temperatures between 200 °C and 1000 °C. Several analytical techniques including X-ray diffraction, X-ray fluorescence, Fourier transform infrared spectroscopy, Differential scanning analysis-Thermogravimetry and Scanning Electron Microscopy were used for the characterization of the produced IPs. Results show that under the optimum synthesis conditions the IPs obtain compressive strength that exceeds 65 MPa. An innovative aspect of this study is that after heating at 400 °C, the specimens acquire compressive strength of 115 MPa and this indicates that they can be also used as fire resistant materials. This study highlights the potential of alkali activation for the valorization of a ferronickel slag and the production of IPs that can be used as binders or in several construction applications, thus improving the sustainability of the metallurgical sector.

Graphene is a popular material with outstanding properties due to its single layer. Graphene and its oxide have been put to the test as nano-sized building components for separation membranes with distinctive structures and adjustable physicochemical attributes. Graphene-based membranes have exhibited excellent water and gas purification abilities, which have garnered the spotlight over the past decade. This work aims to examine the most recent science and engineering cutting-edge advances of graphene-based membranes in regard to design, production and use. Additional effort will be directed towards the breakthroughs in synthesizing graphene and its composites to create various forms of membranes, such as nanoporous layers, laminates and graphene-based compounds. Their efficiency in separating and decontaminating water via different techniques such as cross-linking, layer by layer and coating will also be explored. This review intends to offer comprehensive, up-to-date information that will be useful to scientists of multiple disciplines interested in graphene-based membranes.

In this experimental study, the alkali activation of acid leaching residues using a mixture of sodium hydroxide (NaOH) and alkaline sodium silicate solution (Na₂SiO₃) as activators is investigated. The residues were also calcined at 800 and 1000 °C for 2 h or mixed with metakaolin (MK) in order to increase their reactivity. The effect of several parameters, namely the H₂O/Na₂O and SiO₂/Na₂O ratios present in the activating solution, the pre–curing time (4–24 h), the curing temperature (40–80 °C), the curing time (24 or 48 h), and the ageing period (7–28 days) on the properties of the produced alkali activated materials (AAMs), including compressive strength, porosity, water absorption, and density, was explored. Analytical techniques, namely X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and elemental mapping analysis were used for the identification of the morphology and structure of the final products. The experimental results show that the laterite acid leaching residues cannot be alkali activated in an unaltered state, and the compressive strength of the produced AAMs barely reaches 1.4 MPa, while the mixing of the residues with 10 wt% metakaolin results in noticeably higher compressive strength (41 MPa). Moreover, the calcination of residues at 800 and 1000 °C has practically no beneficial effect on alkali activation. Alkali activated materials produced under the optimum synthesis conditions were subjected to high temperature firing for 2 h and immersed in distilled water or acidic solution (1 mol L⁻¹ HCl) for 7 and 30 days in order to assess their structural integrity under different environmental conditions. This study explores the potential of alkali activation of laterite leaching residues amended with the addition of metakaolin for the production of AAMS that can be used as binders or in several construction applications in order to enable their valorization and also improve the environmental sustainability of the metallurgical sector.

The present study focuses on the optimization of alkali activation of ferronickel (FeNi) slag for the production of alkali-activated materials (AAMs). The effect of the main factors including molarity and SiO₂/Na₂O molar ratio in the activating solution, pre-curing and curing time, curing temperature, and aging period on the compressive strength and other properties of the final products is assessed. Emphasis is paid to the study of the effect of low curing temperature to decrease the overall footprint of alkali activation. Several analytical techniques including X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and Scanning electron microscopy (SEM) are used for the identification of the mineralogy and the morphology of the precursor and the final products. The experimental results indicate that the produced AAMs achieve a maximum compressive strength of 99 MPa using NaOH molarity 8 mol/L (M), SiO₂/Na₂O molar ratio 1, curing temperature 80 °C, curing time 24 h, and aging period 7 days. SEM/EDS–energy dispersive X-ray spectroscopy analysis indicates that alkali activation results in a homogeneous binding phase, characteristic of the expected iron-rich matrix, while the microstructure of the AAMs is characterized by a glassy and smooth surface without the presence of any visible cracks or defects. The produced AAMs may be used as alternative binders for the replacement of cement in the production of concrete or as construction elements.

The phytoremediation potential of the halophytic plant, Tamarix smyrnensis (T. smyrnensis), was examined in toxic metal spoils assisted by biochar and irrigation by air nanobubbles. The substrate (spoil) used in the present study was derived from areas close to laterite (Ni-containing ores) mines. The efficiency of biochar addition in two rates (5 t/ha and 20 t/ha) to improve microbial properties and stabilize soil aggregates was also examined. Furthermore, the effect of irrigation with air-nanobubble-supplemented water was evaluated for the remediation of toxic metal spoils. The physiological condition of the plant species was investigated in terms of biomass, height, chlorophyll content, and antioxidant enzymes. The alkali and heavy metal accumulation and their distribution in the plant parts were assessed to explore whether toxic metals could accumulate in the root and further translocate to the aboveground tissues. The growth of T. smyrnensis was not adversely affected by its cultivation in lateritic spoil, and the highest rate of biochar exhibited a beneficial effect on plant growth in terms of weight (aerial and subterranean biomass). The highest biochar application rate led to significant increases in total chlorophyll content, showing a 97.6% increase when biochar is used alone and a 136% increase when combined with nanobubble irrigation. Remarkably, only when combining irrigation with air nanobubbles and low biochar supplementation did the translocation of the metals from soil to the aboveground tissues occur as the translocation factor was estimated to be greater than unity (TF > 1). The bioconcentration factors remained below 1.0 (BCF < 1) across all treatments, demonstrating limited mobilization from soil to plant tissues despite the application of soil amendments. Finally, the application of nanobubbles increased slightly but not substantially the total uptake of metals, which showed a significant decrease compared to the control groups when the lower dosage of biochar was utilized.