Designing novel antiviral personal protective equipment (PPE) is crucial for preventing viral infections such as COVID-19 in humans. Here, we fabricate an electrospun nanofiber-based Viroblock (VB)-loaded polyacrylonitrile (PAN)/zinc oxide (ZnO) hybrid nanocomposite for PPE applications. Five different concentrations of Viroblock (0.5%, 1.5%, 2.5%, 3.5%, and 5%) were added to PAN/ZnO solution and loaded for electrospinning. The developed samples reflected antibacterial activity of 92.59% and 88.64% against Staphylococcus aureus and Pseudomonas aeruginosa bacteria, respectively, with 5% VB loading. Moreover, a significant reduction in virus titer (37%) was observed with the 5% VB/PAN/ZnO nanofiber sheet. Hence, VB-loaded PAN/ZnO nanofibers have great potential to kill enveloped viruses such as influenzas and coronaviruses and could be the ideal candidate for the development of nanofiber-based PPE, such as facemasks and surgical gowns, which can play a key role in the protection of frontline health workers and the general public in the COVID-19 pandemic.

Due to the ever-growing demand for bast fibres for technical and garment textiles, complementary sources to textile flax, whose cultivation in western Europe cannot really be extended, need to be proposed. In this study, the interest in harvesting and processing linseed flax straw is studied for geotextile applications. The main critical stages of fibre-to-yarn production for geotextiles were investigated. Different dew retting levels as well as different all-fibre extraction processes were investigated to achieve this objective. It was demonstrated that the fibres extracted from linseed flax stems subjected to 12 weeks of dew retting using breaking rollers, thresher and a breaking card exhibited the most suitable morphological and mechanical properties. The optimal fibres were converted into 100% linseed flax yarns using a flyer spinning machine, and the mechanical properties as well as the biodegradability of the linseed yarns were evaluated to understand their potential as geotextiles. These linseed flax yarns were further coated with linseed oil or chitosan to enhance their durability. It was observed that the linseed oil coating better preserved the yarn’s integrity and mechanical properties over time, and it permitted doubling their service life potential.