Zn-doped TiO₂ nanoparticles were successfully fabricated using sonochemical method accompanying post calcination process. Titanium isopropoxide (Ti[OC₃H₇]₄) and Zinc chloride (ZnCl₂) were used as starting precursors for Ti and Zn sources, respectively. The homogeneous mixing solution of different Zn (0–1 mol%) and Ti ratio were irradiated in high intensity ultrasound sonometer (750 W 20 kHz) for 30 min at room temperature to obtain as-synthesized Zn-doped TiO₂ nanoparticles followed by calcination at 400–700°C. To evaluate the structure and phase identification of prepared powders, the X-ray diffraction (XRD) and Raman spectroscopy were employed. The results reveal that the as-synthesized Zn-doped TiO₂ nanoparticles are in anatase phase and their crystallinity increases with increasing calcined temperature. The morphology of as-synthesized powders was investigated by transmission electron microscope (TEM). The effect of Zn content and calcinations temperature on TiO₂ properties was also discussed.

The structural and optical characterizations of nanocomposite films of polymethyl methacrylate (PMMA) and SiO₂/TiO₂ composites prepared via the spin-coating technique were investigated using different SiO₂:TiO₂ ratios. The SiO₂/TiO₂ nanocomposites were synthesized using the sonochemical process with Si:Ti precursor ratios of 1:0.1, 1:0.5, 1:1, 1:2, 1:4, and 0:1. All characterizations of ultrafine SiO₂/TiO₂ particles were loaded at 1 wt.% in a PMMA matrix for the fabrication of transparent SiO₂/TiO₂/PMMA composite films. The phase structure and morphology of SiO₂/TiO₂/PMMA composite films were monitored using X-ray diffraction, optical microscopy, and field-emission scanning electron microscopy. A surface roughness analysis of SiO₂/TiO₂/PMMA nanocomposite films was conducted using atomic force microscopy. For optical characterization, transmission properties with different incident angles of SiO₂/TiO₂/PMMA composite films were analyzed with UV-vis spectrophotometry. The water contact angles of SiO₂/TiO₂/PMMA composite films were analyzed to identify hydrophilic properties on film surfaces. Photocatalytic reactions in SiO₂TiO₂ composite films under UV irradiation were evaluated using rhodamine B dye degradation. The optimal condition of SiO₂/TiO₂/PMMA nanocomposite films was obtained at a 1:1 SiO₂:TiO₂ ratio in self-cleaning applications, resulting from good particle dispersion and the presence of the TiO₂ phase in the composite.