As a typical brittle material, epoxy resin cannot meet its application requirements in specific fields by only considering a single toughening method. In this paper, the effects of carboxyl-terminated polybutylene adipate (CTPBA) and zinc powder on the mechanical properties, adhesion properties, thermodynamic properties and medium resistance of epoxy resin were studied. A silane coupling agent (KH-550) was used to modify zinc powder. It was found that KH-550 could significantly improve the mechanical properties and bonding properties of epoxy resin, and the modification effect of flake zinc powder (f-Zn) was significantly better than that of spherical zinc powder (s-Zn). When the addition amount of f-Zn was 5 phr, the tensile shear strength and peel strength of the composites reached a maximum value of 13.16 MPa and 0.124 kN/m, respectively, which were 15.95% and 55% higher than those without filler. The tensile strength and impact strength reached a maximum value of 43.09 MPa and 7.09 kJ/m², respectively, which were 40.54% and 91.11% higher than those without filler. This study provides scientific support for the preparation of f-Zn-modified epoxy resin.

Polymer matrix solid buoyancy materials (PSBMs) have the advantages of low density, high strength, low cost, and low water absorption, and they are widely used in marine engineering fields. How to improve the performance of PSBMs further and adapt them to harsh marine environments has become a hot topic in current research. This paper provides a comprehensive summary of PSBM, detailing both the preparation methodologies and properties of single-component and multi-component PSBM. In this paper, relevant research is systematically summarized from two dimensions of matrix and filler, and the application of thermosetting resin and thermoplastic resin as a matrix in PSBM is introduced in detail, and the corresponding research on fillers such as hollow glass microspheres, fly ash, hollow ceramic spheres and hollow polymer microspheres are expounded. This paper aims to summarize the latest advancements in PSBM research, thereby providing insights into the current state of the field and guiding future investigations.

With the advantages of high energy density, abundant resources and environmental friendliness, Aqueous Zinc‐ion Batteries (AZIBs) are considered as one of the promising new energy systems. However, its practical application is limited by the problems of irregular dendrite growth and interfacial side reaction in zinc anode. In view of the above problems, relevant researchers have given solutions such as the construction of artificial protective layer and the regulation of substrate structure. This paper summarizes the relevant literatures in order to help the future research of zinc‐ion batteries.

To enhance the damping properties of nitrile butadiene rubber (NBR), the elastomer used was blended with chlorinated paraffin 52 (CP52) to prepare NBR/CP52 composites. The results showed that CP52 could significantly enhance the damping properties of NBR and shift the glass transition temperature (T_g) to lower temperatures. Molecular dynamics models of the CP52/NBR system were established, and the damping properties of the CP52-reinforced NBR were investigated using molecular dynamics (MD) simulations. Through the combination of MD simulations and the experimental results, the essential mechanism of the enhanced damping properties of the NBR was methodically expatiated and was ascribed to the Cl-CP-H····NC-NBR (type I) and CP-Cl····H-NBR-CN (type II) analogous hydrogen bonds formed between NBR and CP52. The higher the CP52 content, the higher the analogous hydrogen bond concentration, and the better the damping properties of the CP52/NBR composites. The experimental results were very consistent with the MD simulation results, meaning that the combination method can provide a new means to optimize the design of damping materials and broaden the application range of small polar molecules in the damping modification of polar rubber materials.