As a typical brittle material, epoxy resin cannot meet its application requirements in specific fields by only considering a single toughening method. In this paper, the effects of carboxyl-terminated polybutylene adipate (CTPBA) and zinc powder on the mechanical properties, adhesion properties, thermodynamic properties and medium resistance of epoxy resin were studied. A silane coupling agent (KH-550) was used to modify zinc powder. It was found that KH-550 could significantly improve the mechanical properties and bonding properties of epoxy resin, and the modification effect of flake zinc powder (f-Zn) was significantly better than that of spherical zinc powder (s-Zn). When the addition amount of f-Zn was 5 phr, the tensile shear strength and peel strength of the composites reached a maximum value of 13.16 MPa and 0.124 kN/m, respectively, which were 15.95% and 55% higher than those without filler. The tensile strength and impact strength reached a maximum value of 43.09 MPa and 7.09 kJ/m², respectively, which were 40.54% and 91.11% higher than those without filler. This study provides scientific support for the preparation of f-Zn-modified epoxy resin.

Cathodic protection is widely used for metal corrosion protection. To improve their performance, it is necessary and urgent to study the influence of metal oxides on the microstructure and performance of aluminum alloy sacrificial anodes. Taking an Al-Ga-In sacrificial anode as the research object, the dissolution morphology and current efficiency characteristics were studied by means of electrochemical testing and microstructural observation, and the influence of varying Pb and Bi contents on the performance of an aluminum alloy sacrificial anode was investigated. The test results reveal that: (1) The Al-Ga-In sacrificial anode with 4% Pb and 1% Bi contents exhibits the best sacrificial anode performance. (2) The inclusion of an appropriate Bi element content shifts the open-circuit potential in a negative direction and promotes activation dissolution. Conversely, excessive Bi content leads to uneven dissolution, resulting in the shedding of anode grains and greatly reducing the current efficiency. (3) During the activation dissolution of the aluminum alloy, the second phase preferentially dissolves, and the activation point destroys the oxide film, resulting in the dissolution of the exposed aluminum matrix. Consequently, the concentration of dissolved metal ions is reduced and deposited back on the surface of the anode sample, promoting the continuous dissolution of the anode.