In this study, hybrid nanocomposites consisting of Fe₃O₄/BaTiO₃/epoxy resin were prepared with varying amounts of filer content. Structural and morphological characterization, conducted via X-Ray Diffraction patterns and Scanning Electron Microscopy images, revealed the successful fabrication of composites and fine dispersion of inclusions. Thermomechanical properties are studied via Differential Scanning Calorimetry, Thermogravimetric Analysis, Dynamic Mechanical Analysis and static mechanical tests. Hybrid composites exhibit enhanced thermal stability and improved mechanical response. Indicatively, Young’s modulus, tensile strength and fracture toughness increase from 1.26 GPa, 22.25 MPa, and 3.03 kJ/m³ for the neat epoxy to 1.39 GPa, 45.73 MPa, and 41.08 kJ/m³ for the composites with 20 or 15 parts per hundred resin per mass (phr) of Fe₃O₄, respectively. Electrical behavior is investigated via Broadband Dielectric Spectroscopy and ac conductivity measurements. The real part of dielectric permittivity reaches the value of 11.11 at 30 °C for the composite with 40 phr of Fe₃O₄. The ability to store and retrieve electric energy on the nanocomposites is examined with the following parameters: the filler content and the applied voltage under dc conditions. Retrieved energy reaches 79.23% of the stored one, for the system with 15 phr of Fe₃O₄. Magnetic response is studied via a Vibrating Sample Magnetometer. Magnetic saturation, for the system with the highest magnetic filler content, obtains the value of 25.38 Am²/kg, while pure magnetic powder attains the value of 86.75 Am²/kg. Finally, the multifunctional performance of the nanocomposites is assessed regarding all the exerted stimuli and the optimum behavior is discussed.

Polymer matrix nanocomposites are widely studied because of the versatility of their physical and mechanical properties. When these properties are present simultaneously, responding at relative stimuli, multifunctional performance is achieved. In this study, hybrid nanocomposites of SrFe₁₂O₁₉ and BaTiO₃ ceramic particles dispersed in an epoxy resin matrix were fabricated and characterized. The content of SrFe₁₂O₁₉ was varying, while the amount of BaTiO₃ was kept constant. The successful fabrication of the nanocomposites and the fine dispersion of the ceramic particles was verified via the morphological and structural characterization carried out with X-ray Diffraction patterns and Scanning Electron Microscopy images. Dielectric response and related relaxation phenomena were studied by means of Broadband Dielectric Spectroscopy. Dielectric permittivity augments with filler content, while the recorded relaxations, with descending relaxation time, are: (i) interfacial polarization, (ii) glass-to-rubber transition, (iii) intermediate dipolar effect, and (iv) re-orientation of polar-side groups of the main polymer chain. SrFe₁₂O₁₉ nanoparticles induce magnetic properties to the nanocomposites, which alter with the magnetic filler content. Static and dynamic mechanical response improves with filler content. Thermogravimetric analysis shown that ceramic particles are beneficial to the nanocomposites’ thermal stability. Glass transition temperature, determined via Differential Scanning Calorimetry, was found to slightly vary with filler content, in accordance with the results from dynamic mechanical and dielectric analysis, indicating the effect of interactions occurring between the constituents. Examined systems are suitable for energy storing/retrieving.

In this work magnetic nanoparticles (Fe₃O₄, or ZnFe₂O₄, or SrFe₁₂O₁₉) and BaTiO₃ microparticles were embedded in an epoxy resin for the synthesis of three series of hybrid magnetic polymer nanocomposites. Barium titanate content was kept constant, while magnetic phase content was varied. Fabricated specimens were structurally and morphologically characterized by employing scanning electron microscopy images and X-ray diffraction patterns. Results implied successful synthesis of the hybrid nanocomposites. The magnetic behavior of the pure magnetic nanoparticles and the fabricated nanocomposites was investigated via a Vibrating Sample Magnetometer. The magnetic performance of each type of magnetic phase (i.e., soft and hard) was induced in the nanocomposites, and magnetic performance is strengthened with the increase in magnetic phase content. Initial magnetization curves were used for the determination of mass magnetic susceptibility of all nanocomposites. Magnetic saturation and magnetic remanence have been found to follow a linear relationship with magnetic phase content, giving the opportunity to predict the system’s response in advance.