White ultra-high-performance concrete (WUHPC) performed outstanding mechanical, durability, and aesthetical properties, which was preferred in infrastructure to avoid the secondary painting, decrease the maintenance, and prolong the service life. Supplementary cementitious materials (SCMs) were often used in WUHPC to reduce the environment impacts and material costs. In this study, limestone powder (LP), metakaolin (MK), and silica fume (SF) were used as SCMs to largely substitute white Portland cement (WPC) to prepare WUHPC, the effects of substituted ratio on flowability, strength, and whiteness were studied, and the hydration products were also analyzed by quantitative-XRD method and SEM. The whiteness was calculated in chromatic space CIELAB by measuring tristimulus values of L, a*, and b*, and the controlled factor on whiteness was also investigated. As the results, the WUHPC with compressive strength exceeded 150 MPa and whiteness over 90 was prepared with WPC substitution of 35~65%. The SF improved the flowability and strength about 10% due to its filling and ball effect, while the irregular particle sharp and non-uniform size distribution of MK caused the reversed development. The increased dosage of raw materials with higher L value, such as LP and MK, made the WUHPC whiter. The hydration products with varied SCMs ratio were in the same category by different content. It was supposed that CaCO₃ and C-S-H gel in hydration products caused higher whiteness, while C₃S, CaMg(CO₃)₂, and SiO₂ were against the whiteness. The results proved that with a large fraction of SCMs, the WUHPC with high strength and good appearance were prepared, and the whiteness of WUHPC were both controlled by the raw materials and the content of hydration products.

Ultra-high-performance concrete (UHPC) has greater mechanical and durability performance than normal concrete (NC). Using a limited dosage of UHPC on the external surface of NC to form a gradient structure could significantly improve the strength and corrosion resistance of the concrete structure and avoid the problems caused by bulk UHPC. In this work, white ultra-high-performance concrete (WUHPC) was selected as an external protection layer for normal concrete to construct the gradient structure. WUHPC of different strengths were prepared, and 27 gradient WUHPC-NC specimens with different WUHPC strengths and interval times of 0, 10, and 20 h were tested using splitting tensile strength to reveal the bonding properties. Fifteen prism gradient specimens with the size of 100 × 100 × 400 mm and a WUHPC ratio of 1:1, 1:3, and 1:4 were tested using the four-pointed bending method to study the bending performance of the gradient concrete with different WUHPC thicknesses. Finite element models with different WUHPC thicknesses were also built to simulate the cracking behaviors. The results showed that the bonding properties of WUHPC-NC were stronger with less interval time and reached the maximum of 1.5 MPa when the interval was 0 h. Moreover, the bond strength first increased and then decreased with the decline in the strength gap between WUHPC and NC. When the thickness ratios of WUHPC to NC were 1:4, 1:3, and 1:1, the flexural strength of the gradient concrete improved by 89.82%, 78.80%, and 83.31%, respectively. The major cracks rapidly propagated from the 2 cm position to the bottom of the mid-span, and the thickness of 1:4 was the most efficient design. The results simulated by finite element analysis also proved that the elastic strain at the crack propagating point was the minimum and was easier to crack. The simulated results were in good accordance with the experimental phenomenon.