Most of the dental materials available on the market are still based on traditional monomers such as bisphenol A-glycidyl methacrylate (Bis-GMA), urethane dimethacrylate (UDMA), triethyleneglycol dimethacrylate (TEGDMA), and ethoxylated bisphenol-A dimethacrylate (Bis-EMA). The interactions that arise in the monomer mixture and the characteristics of the resulting polymer network are the most important factors, which define the final properties of dental materials. The use of three different monomers in proper proportions may create a strong polymer matrix. In this paper, fourteen resin materials, based on urethane dimethacrylate with different co-monomers such as Bis-GMA or Bis-EMA, were evaluated. TEGDMA was used as the diluting monomer. The flexural strength (FS), diametral tensile strength (DTS), and hardness (HV) were determined. The impacts of material composition on the water absorption and dissolution were evaluated as well. The highest FS was 89.5 MPa, while the lowest was 69.7 MPa. The median DTS for the tested materials was found to range from 20 to 30 MPa. The hardness of the tested materials ranged from 14 to 16 HV. UDMA/TEGDMA matrices were characterized by the highest adsorption values. The overall results indicated that changes in the materials’ properties are not strictly proportional to the material’s compositional changes. The matrices showed good properties when the composite contained an equal mixture of Bis-GMA/Bis-EMA and UDMA or the content of the UDMA monomer was higher.

The aim of this article was to compare the biomechanical properties of commercial composites containing different photoinitiators: Filtek Ultimate (3M ESPE) containing camphorquinone (CQ); Estelite Σ Quick (Tokuyama Dental) with CQ in RAP Technology^®; Tetric EvoCeram Bleach BLXL (Ivoclar Vivadent AG) with CQ and Lucirin TPO; and Tetric Evoceram Powerfill IVB (Ivoclar Vivadent AG) with CQ and Ivocerin TPO. All samples were cured with a polywave Valo Lamp (Ultradent Products Inc.) with 1450 mW/cm². The microhardness, hardness by Vicker’s method, diametral tensile strength, flexural strength and contraction stress with photoelastic analysis were tested. The highest hardness and microhardness were observed for Filtek Ultimate (93.82 ± 17.44 HV), but other composites also displayed sufficient values (from 52 ± 3.92 to 58,82 ± 7.33 HV). Filtek Ultimate not only demonstrated the highest DTS (48.03 ± 5.97 MPa) and FS (87.32 ± 19.03 MPa) but also the highest contraction stress (13.7 ± 0.4 MPa) during polymerization. The TetricEvoCeram Powerfill has optimal microhardness (54.27 ± 4.1 HV), DTS (32.5 ± 5.29 MPa) and FS (79.3 ± 14.37 MPa) and the lowest contraction stress (7.4 ± 1 MPa) during photopolymerization. To summarize, Filtek Ultimate demonstrated the highest microhardness, FS and DTS values; however, composites with additional photoinitiators such as Lucirin TPO and Ivocerin have the lowest polymerization shrinkage. These composites also have higher FS and DTS and microhardness than material containing CQ in Rap Technology.

Due to its unique properties, zirconia is increasingly being used in dentistry, but surface preparation for bonding is difficult because of its polycrystalline structure. This study aimed to determine the effect of a new etching technique (Zircos-E) on Ceramill Zi (Amann Girrbach). The effect of etching and the use of primers (Monobond Plus and MKZ Primer) on the bond strength of zirconia with resin cement (NX3) was assessed. Shear bond strength was evaluated after storage in water for 24 h and after thermal aging (5000 thermocycling at 5 °C/55 °C). A scanning electron microscope (Hitachi S-4700) was used to evaluate the surface structure before and after the Zircos-E system. The roughness parameters were assessed using an SJ-410 profilometer. The etched zirconia surface is more homogeneous over the entire surface, but some localized forms of erosion exist. The etching of zirconia ceramics caused changes in the surface structure of zirconia and a significant increase in the shear bond strength between zirconia and resin cement. The use of primers positively affects the adhesion between resin cement and zirconia. Aging with thermocycler significantly reduced the shear bond strength, with one exception—sandblasted samples with MKZ Primer. Standard ceramic surface preparation, involving only alumina sandblasting, does not provide a satisfactory bond. The use of etching with the Zircos-E system and primers had a positive effect on the strength of the zirconium–resin cement connection.

Materials with potential use as dental restoration should be evaluated in an aggressive environment. Such accelerated aging is widely used in other industries and allows the assessment of service life. In the presented study, three neat resins (UDMA/Bis-GMA/TEGDMA 70/10/20 wt.%, UDMA/Bis-GMA/TEGDMA 40/40/20 wt.% and UDMA/Bis-EMA/TEGDMA 40/40/20 wt.%) and three composites based on these matrices were tested before and after aging protocols (I-7500 cycles, 5 °C and 55 °C, water and 7 days, 60 °C, 0.1 M NaOH; II-5 days, 55 °C, water and 7 days, 60 °C, 0.1 M NaOH). Flexural strength (FS), diametral tensile strength (DTS) and hardness (HV) were determined. Applied aging protocols resulted in a decrease in the value of the FS, DTS and HV. Larger changes were noticed for the neat resins. Materials in which the content of bis-GMA was lower or substituted by bis-EMA showed better resistance to degradation. The choice of mixtures with monomers characterized by lower sorption values may favorably affect hydrolytic stability. It was shown that for composites there was a drastic decrease in hardness, which suggests a more superficial effect of the used protocols. However, degradation of the surface layer can result in a growing problem over time given that the mastication processes are an inherent element in the oral environment.

In restorative dentistry, there are no standardized in vitro accelerated aging methods to evaluate the long-term stability of dental composites. Current research aimed at extending the clinical success of restorations emphasizes the need for post-aging evaluation. This study represents the final stage of assessing three selected aging protocols that utilize a 0.1 M sodium hydroxide solution as the primary agent to accelerate degradation processes. Twelve resin-based composites, categorized into five types, were evaluated for flexural strength (FS), diametral tensile strength (DTS), hardness (HV), and fracture toughness (FT) both before and after aging. The proposed aging methods significantly degraded the mechanical properties of most materials, highlighting the effectiveness of 0.1 M NaOH as a medium for hydrolytic stability testing. Materials with a high filler content (approximately 80 wt.%) were notably prone to degradation, underscoring the importance of optimizing the filler and coupling agent. The findings suggest that incorporating thermocycling into aging protocols may enhance the development and evaluation of innovative dental composites. This work contributes to establishing a foundation for standardized aging protocols, supporting the accurate assessment of composites in vitro.

The aim of this research was to compare the biomechanical properties of experimental composites containing a classic photoinitiating system (camphorquinone and 2-(dimethylami-no)ethyl methacrylate) or diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO) as a photoinitiator. The produced light-cured composites consisted of an organic matrix-Bis-GMA (60 wt.%), TEGDMA (40 wt.%) and silanized silica filler (45 wt.%). Composites contained 0.27; 0.5; 0.75 or 1 wt.% TPO. Vickers hardness, microhardness (in the nanoindentation test), diametral tensile strength, resistance to three-point bending and the CIE L* a* b* colorimetric analysis was performed with each composite produced. The highest average Vickers hardness values were obtained for the composite containing 1 wt.% TPO (43.18 ± 1.7HV). The diametral tensile strength remains on regardless of the type and amount of photoinitiator statistically the same level, except for the composite containing 0.5 wt.% TPO for which DTS = 22.70 ± 4.7 MPa and is the lowest recorded value. The highest average diametral tensile strength was obtained for the composite containing 0.75 wt.% TPO (29.73 ± 4.8 MPa). The highest modulus of elasticity characterized the composite containing 0.75 wt.% TPO (5383.33 ± 1067.1 MPa). Composite containing 0.75 wt.% TPO has optimal results in terms of Vickers hardness, diametral tensile strength, flexural strength and modulus of elasticity. Moreover, these results are better than the parameters characterizing the composite containing the CQ/DMAEMA system. In terms of an aesthetic composite containing 0.75 wt.%. TPO is less yellow in color than the composite containing CQ/DMAEMA. This conclusion was objectively confirmed by test CIE L* a* b*.