AISI 304 SS has good corrosion resistance in a variety of environments but does not have good resistance to wear. Aggressive marine environments require materials that can withstand both the biocorrosion and the wear associated with the impact of waves, ocean currents and suspended particles. Oxy-nitriding of stainless steels can be used to increase their hardness and wear resistance. The conventional oxy-nitriding process is lengthy, and the temperature involved can affect the corrosion resistance of the material. To mitigate these problems, it was decided to study an oxy-nitriding process in plasma electrolytic conditions, using aqueous solutions of 20, 30 and 40 wt% urea. The results showed that all the concentrations evaluated gave lower levels of wear than untreated stainless steel. However, considering the amount of urea used and the environmental emissions from the waste generated, a concentration of 20% by weight of urea in the electrolyte is considered sufficient to increase up to three times the wear resistance of stainless steel. XRD, XPS and microscopy analyses showed that, in the main, the outermost layer of the steel surface treated by electrolytic plasma has a morphology of small craters of chromium and iron oxy-nitrides. A nitrogen diffusion layer was also seen below the oxy-nitrided layer.

Aims: This work uses the MACE method to synthesize SiNWs- NiNPs/NiONPs to degrade organic pollutants by photocatalysis. Background: Photocatalytic degradation has been applied as an attractive solution to remove several organic pollutants. Heterostructured nanomaterials have become an interesting platform for investigation. Metal-assisted chemical etching (MACE) stands out as a promising technique because it is simple, low cost, and fast. Objective: Attain the degradation of methyl orange (MO) in the presence of silicon nanowires (SiNWs) in heterojunction with Nickel/Nickel Oxide nanoparticles (NiNPs-NiONPs). Methods: SiNWs were synthesized by metal (Ag) assisted chemical etching (MACE) of monocrystalline silicon wafers. NiNPs were non-electrolytically deposited on the SiNWs (electroless method). The morphology of the SiNWs- NiNPs/NiONPs was observed by SEM. Results: Heterogeneous photocatalytic degradation of methyl orange (C14H14N3NaO3S) in an aqueous solution at a concentration of 20 ppm had an efficiency of 66.5% after 180 min under UV irradiation. The MO degradation percentage was determined using UV-visible spectrophotometry. Conclusion: The SiNWs-NiNPs/NiONPs were obtained composed mainly of Si covered by SiO2 decorated on the tips with Ni (II) in the form of NiO and a small amount of nickel metal. The removal efficiency obtained at 180 min of light exposure was 66.5%. After the photocatalysis tests, further oxidation of the NiNPS into NiONPS, was attributed to the reactive oxygen species in the aqueous medium based on the changes of the oxygen and Ni2p3/2 peaks by XPS. Other: Through XPS, the oxidation state of the SiNWs- NiNPs/NiONPs was analyzed.

Geopolymers have been mainly utilized as structural materials; their chemical structure and morphologies have been explored for their potential as a high-performance material in emerging applications. Geopolymer composites reinforced with materials based on agro-waste are attracting interest in engineering applications due to their easy processing, low cost, low density, and high strength-to-weight ratio. This investigation pursues an experimental methodology that consists of a scheme to make composites with a geopolymer matrix and agro-waste (rice husk, barley, and coffee) as aggregate material, that can be applied in various fields of construction. The study was intended to determine the influence of adding various agro-wastes on the mechanical properties of the geopolymer. According to the respective ASTM standards, the materials obtained were prepared and analyzed to determine their compressive strength, flexural strength, hardness and scanning electron microscopy (SEM)-determined characteristics. The results revealed that, for the compression tests, the composites formed by a sol-gel matrix and barley husk showed a better yield, obtaining the highest value of 3.5 N/mm². Concerning hardness testing, the composites with a geopolymer matrix and coffee husks obtained higher values compared to the other composites. For the flexural tests, the compounds with the sol-gel/fly ash matrix obtained the highest yield stress value, which was 5.25 MPa with an elastic modulus of 7.59 GPa. The results of the microstructural analysis showed good husk-matrix interaction, together with failure mechanisms. The conformation of such waste-based compounds may enable them to replace natural wood in some applications, such as in the finishing of interiors of homes, during the final stages in the construction of buildings, or in the decoration of inhabited houses, as well as in finishing in the manufacture of furniture.

The lifetime of mirrors in outdoor conditions is crucial in the correct operation of any concentrating solar power (CSP) installation. In this work, the corrosion behavior of two types of metallized surfaces was studied. The first was made of a flexible polymer having a deposited reflective silver metallic film. The second was made of the same surface type with a dielectric SiO₂ protection coating by an atmospheric pressure plasma jet. Polycarbonate sheets were used as substrates on which metallic silver was deposited by the Dynamic Chemical Deposit technique. This electroless technique allowed producing the mirror finishing under environmental conditions by sequentially spraying; as aerosols projected towards the substrate surface, the activation and reducing-oxidizing solutions with rinsing after each one. The silver coatings were about 100 nm thick. Environmental and accelerated weathering degradation and salt and sulfide fogs were carried out. XPS analyses show that the corrosion products formed were Ag₂S, AgCl, and Ag₂O. It was observed that the tarnishing was initiated locally by the formation of Ag₂S columns as eruptions on the surface. Subsequently, the ions diffused through the protective layer and into the silver reflective layer, chemically reacting with the silver. The main atmospheric agents were H₂S, chloride particles, and HCl. High reflectance was initially obtained of about 95%. The obtained results suggest mechanisms for the degradation of exposed silver surfaces to moisturized atmospheres with corrosive compounds.