Although many attempts have been made in previous research to identify the various parameters governing the rheology of cement paste, there has been little progress in evaluating the combined effects of these parameters. In this paper, a new parameter, the excess water to solid surface area ratio, is proposed to evaluate the combined effects of water content, packing density, and solid surface area on the rheological properties of cement paste. For the purpose of determining the value of this new parameter, a new wet packing method has been developed to measure the packing density of cementitious materials so that the voids content of the cementitious materials and the amount of excess water in the cement paste can be quantified. A number of cement paste samples containing different proportions of cement, pulverized fuel ash and condensed silica fume, and different water contents have been tested and their rheological properties, as measured by a rheometer, correlated to the new parameter. The correlation...

In the mortar portion of a concrete mix, the water must be more than sufficient to fill the voids between the solid particles of cement and fine aggregate whereas the paste volume must be more than sufficient to fill the voids between the solid particles of fine aggregate so that there will be excess water to form water films coating all the solid particles and excess paste to form paste films coating the fine aggregate particles. Hence, it may be postulated that the water film thickness (WFT) and the paste film thickness (PFT) have major effects on the rheology of mortar. In this study, the combined effects of WFT and PFT on the rheology, cohesiveness and adhesiveness of mortar were investigated by testing mortar samples with varying water, cement and aggregate contents. It was found that whilst the WFT is the single most important factor governing the rheology of mortar, the PFT also has significant effects. Particularly, the PFT has certain interesting effects on the cohesiveness and adhesiveness of mortar, which should be duly considered in mortar design. © 2012 The Author(s).published_or_final_versionSpringer Open Choice, 25 May 201

A high-performance concrete (HPC) is required to have superior performance in various aspects such as workability, strength, durability, dimensional stabil