This research was aimed at developing a dental prototype from 3D printing technology using a synthetic filament of polylactic acid (PLA) and zirconium dioxide (ZrO₂) with glycerol and silane coupling agent as a binder. A face-centered central composite design was used to study the effects of the filament extrusion parameters and the 3D printing parameters. Tensile and compressive testing was conducted to determine the stress-strain relationship of the filaments. The yield strength, elongation percentage and Young’s modulus were also calculated. Results showed the melting temperature of 193 °C, ZrO₂ ratio of 17 wt.% and 25 rpm screw speed contributed to the highest ultimate tensile strength of the synthetic filament. A Nozzle temperature of 210 °C and an infill density of 100% had the most effect on the ultimate compressive strength whilst the printing speed had no significant effects. Differential scanning calorimetry (DSC) was used to study the thermal properties and percentage of crystallinity of PLA filaments. The addition of glycerol and a silane coupling agent increased the tensile strength and filament size. The ZrO₂ particles induced the crystallization of the PLA matrix. A higher crystallization was also obtained from the annealing treatment resulting in the greater thermal resistance performance of the dental crown prototype.

The study aimed to investigate the effects of two different plasma systems, including pinhole plasma jet and gliding arc (GA) plasma, for the degradation of herbicide, diuron, in plasma activated solutions (PAS). In the GA plasma system, air was used to generate plasma, however, Ar, oxygen and nitrogen at different gas compositions were compared in the pinhole plasma jet system. The Taguchi design model was used to study the effects of gas compositions. Results revealed that the pinhole plasma jet system was able to degrade over 50% of the diuron in 60 minutes. The optimal plasma generation condition for the highest degradation of diuron used pure Ar gas. The highest degradation percentage of herbicide in PAS corresponded to the lowest hydrogen peroxide (H₂O₂) content, nitrite concentration and electrical conductivity (EC) of the PAS. The diuron degradation products were identified as 3,4-dichloro-benzenamine, 1-chloro-3-isocyanato-benzene and 1-chloro-4-isocyanato-benzene via gas chromatography-mass spectrometry (GC-MS). The GA plasma system was not adequate for the degradation of herbicide in PAS.