This study aims to address the issues posed by frost damage to concrete structures in cold regions, focusing on reinforcement and repair methods to increase the service life of existing structures instead of costly reconstruction solutions. Due to the limitations of conventional concrete in terms of durability and strength, this research focused on ultra-high-performance concrete (UHPC) by replacing part of the cement with recycled brick powder (RBP) to strengthen ordinary C50 concrete, obtaining UHPC-NC specimens. Mechanical tests investigated the bonding performance of UHPC-NC specimens under various conditions, including interface agents, surface roughness treatments, and freeze–thaw after 0, 50, 100, and 150 cycles with a 30% replacement rate of RBP. Additionally, a multi-factor calculation formula for interface bonding strength was established according to the test data, and the bonding mechanism and model were analyzed through an SEM test. The results indicate that the interface bonding of UHPC-NC specimens decreased during salt freezing compared to hydro-freezing, causing more severe damage. However, the relative index of splitting tensile strength for cement paste specimens showed increases of 14.01% and 14.97%, respectively, compared to specimens without an interface agent. Using an interface agent improved bonding strength and cohesiveness. The UHPC-NC bonding model without an interfacial agent can be characterized using a three-zone model. After applying an interfacial agent, the model can be characterized by a three-zone, three-layer bonding model. Overall, the RBP-UHPC-reinforced C50 for damaged concrete showed excellent interfacial bonding and frost resistance performance.

Using waste clay brick powder (RBP) to partially replace cement in the preparation of concrete, is one way to recycle construction waste. In order to investigate the physical and mechanical properties and volume stability of recycled micropowder ultra-high-performance concrete (UHPC), the basic mechanical and shrinkage properties of recycled micropowder UHPC were studied at replacement rates of 10%, 20%, 30%, 40% and 50%. The results show that: (1) When the activated recycled brick powder is used to replace the cement, the compressive strength, flexural strength and splitting tensile strength of the UHPC initially increase and then decrease with the increase in the substitution rate. When the substitution rate is 10%, the 28 d compressive strength, flexural strength and splitting tensile strength of the UHPC are the highest; (2) Replacing cement with recycled brick powder can reduce the autogenous shrinkage of the UHPC, and the autogenous shrinkage rate of the UHPC decreases with the increase in the brick powder replacement rate. The drying shrinkage of the UHPC can be reduced by replacing cement with recycled brick powder. The drying shrinkage of the UHPC initially decreases, and then increases, with the increase in the replacement rate of brick powder. When the replacement rate of the brick powder was 30%, the drying shrinkage of the UHPC was the least, and this was 49.7% lower than that in the benchmark group. The prediction models of autogenous shrinkage and drying shrinkage are in good agreement with the experimental results, which can be used to predict the shrinkage development of recycled brick powder UHPC.