The maintenance of affected dentin can promote the greater conservation of tooth structure. The development of materials that have properties capable of reducing the demineralizing potential and/or even helping in dental remineralization is important for conservative dentistry. This study aimed to evaluate, in vitro, the alkalizing potential, fluoride as well as calcium ion release ability, antimicrobial activity, and dentin remineralization properties of resin-modified glass ionomer cement (RMGIC) incorporated with a bioactive filler (niobium phosphate (NbG) and bioglass (45S5)). The study samples were grouped into RMGIC, NbG, and 45S5. The materials’ alkalizing potential, ability to release calcium as well as fluoride ions, and antimicrobial properties concerning Streptococcus mutans UA159 biofilms were analyzed. The remineralization potential was evaluated using the Knoop microhardness test, which was performed at different depths. The alkalizing and fluoride release potential was higher for the 45S5 group (p < 0.001) over time. An increase in the microhardness of demineralized dentin was observed in the 45S5 and NbG groups (p < 0.001). No differences in biofilm formation were observed between the bioactive materials, although 45S5 exhibited lower biofilm acidogenicity at different time points (p < 0.001) and greater calcium ion release in the microbial environment. A resin-modified glass ionomer cement enriched with bioactive glasses, particularly 45S5, is a promising alternative for the treatment of demineralized dentin.

To evaluate the influence of the association of the universal adhesive system to different energy densities of the Nd:YAG laser on the hydraulic conductance of dentin. Fifty bovine dentin discs were made. The samples were stratified into four groups (n = 10) according to the treatment performed; SBU- Adper Single Bond Universal (3M ESPE), SBU_60 - SBU associated with the Nd:YAG laser (60mJ, 10Hz, 0.6W - 47.77 J / cm²), SBU_80 - SBU associated with the Nd:YAG laser (80mJ, 10Hz, 0.8 W - 63.69 J / cm2) and C – dentin without treatment (smear layer). Hydraulic conductance measurements were taken 24 hours after the treatments (HC1) and after erosive challenge (HC2). Scanning electron microscopy (SEM) and energy dispersive X-ray spectrometry (EDX) helped to visualize the dentin after the different treatments. Scheffe and Games-Howell statistical tests were used to analyze hydraulic conductance (α = 0.05). The treated dentin (SBU, SBU_60, and SBU_80) reduced HC1 when compared to dentin with smear layer (C) (p< 0.001). The erosive challenge has increased HC2 in SBU_60 and C (p< 0.001), and did not promote a significant difference in SBU_80 and SBU. The SEM / EDX analyzes showed an irregular and semi-permeable barrier on the surfaces of the treated dentin. The association of universal adhesive with Nd:YAG can be an effective alternative for the occlusion of dentinal tubules, whereas higher energy per pulse Nd:YAG (SBU_80) can increase the resistance to permeability when exposed to the erosive challenge. Key words:Dentin, permeability of dentin, Nd:YAG Laser, adhesives.