Cross-linked starch nanocapsules (NCs) were synthesized by interfacial polymerization carried out using the inverse mini-emulsion technique. 2,4-toluene diisocyanate (TDI) was used as the cross-linker. The influence of TDI concentrations on the polymeric shell, particle size, and encapsulation efficiency of a hydrophilic dye, sulforhodamine 101 (SR 101), was investigated by Fourier transform infrared (FT-IR) spectroscopy, dynamic light scattering (DLS), and fluorescence measurements, respectively. The final NC morphology was confirmed by scanning electron microscopy. The leakage of SR 101 through the shell of NCs was monitored at 37 °C for seven days, and afterwards the NCs were redispersed in water. Depending on cross-linker content, permeable and impermeable NCs shell could be designed. Enzyme-triggered release of SR 101 through impermeable NC shells was investigated using UV spectroscopy with different α-amylase concentrations. Impermeable NCs shell were able to release their cargo upon addition of amylase, being suitable for a drug delivery system of hydrophilic compounds.

Encapsulated magnetic nanoparticles are of increasing interest for biomedical applications. However, up to now, it is still not possible to characterize their localized magnetic properties within the capsules. Magnetic Force Microscopy (MFM) has proved to be a suitable technique to image magnetic nanoparticles at ambient conditions revealing information about the spatial distribution and the magnetic properties of the nanoparticles simultaneously. However, MFM measurements on magnetic nanoparticles lead to falsifications of the magnetic MFM signal due to the topographic crosstalk. The origin of the topographic crosstalk in MFM has been proven to be capacitive coupling effects due to distance change between the substrate and tip measuring above the nanoparticle. In this paper, we present data fusion of the topography measurements of Atomic Force Microscopy (AFM) and the phase image of MFM measurements in combination with the theory of capacitive coupling in order to eliminate the topographic crosstalk in the phase image. This method offers a novel approach for the magnetic visualization of encapsulated magnetic nanoparticles.

The combination of several active substances into one carrier is often limited due to solubility, stability and phase‐separation issues. These issues have been addressed by an innovative capsule design, in which nanocapsules are assembled on the microcapsule surface by electrostatic forces to form a pH‐responsive hierarchical capsule@capsule system. Here, melamine‐formaldehyde (MF) microcapsules with a negative surface charge were synthesized and coated with a novel MF‐polyethyleneimine (PEI) copolymer to achieve a positive charge of ζ=+28 mV. This novel coating procedure allows the electrostatic assembly of negatively charged poly‐l‐lactide (PLLA, ζ=−19 mV) and poly‐(lactide‐co‐glycolide) (PLGA, ζ=−56 mV) nanocapsules on the microcapsule surface. Assembly studies at pH 7 gave a partial surface coverage of PLLA nanocapsules and full surface coverage for PLGA nanocapsules. The pH‐responsive adsorption and desorption of nanocapsules was shown at pH 7 and pH 3.

Encapsulation of volatile organic compounds (VOCs) that could evaporate at a defined rate is of immense interest for application in emission reference materials (ERMs). Polyurethane/polyurea microcapsules with various VOC active ingredients (limonene, pinene, and toluene) were successfully produced by interfacial polymerization with Shirasu porous glass membrane emulsification in a size range between 10 and 50 mu m. The effect of surfactant, VOC, monomer(s) type, and ratio has a great effect on the formulation process and morphology of capsules. The type of VOC played a significant role in the encapsulation efficiency. Due to the difference in vapor pressure and VOC/water interfacial tension, the formulation for encapsulation was optimized for each individual VOC. Furthermore, to achieve effective stability of the large droplets/capsules, a combination of ionic and nonionic surfactants was used. Optical and scanning electron microscopy, Fourier transform infrared spectroscopy (FTIR), and thermogravimetric analysis (TGA), were used to characterize the optimized microcapsules. The results showed that the obtained microcapsules exhibited a spherical shape and core-shell morphology and featured characteristic urethane-urea bonds. The amount of encapsulated VOC ranges between 54 and 7 wt %. The emission tests were performed with the help of the emission test chamber procedure (EN 16516). The limonene-loaded polyurethane/polyurea microcapsules show a change in emission rate of less than 10% within 14 days and can be considered as a potential candidate for use as an ERM.