Titanium and stainless steel are commonly known as osteosynthesis materials with high strength and good biocompatibility. However, they have the big disadvantage that a second operation for hardware removal is necessary. Although resorbable systems made of polymers or magnesium are increasingly used, they show some severe adverse foreign body reactions or unsatisfying degradation behavior. Therefore, we started to investigate molybdenum as a potential new biodegradable material for osteosynthesis in craniomaxillofacial surgery. To characterize molybdenum as a biocompatible material, we performed in vitro assays in accordance with ISO Norm 10993-5. In four different experimental setups, we showed that pure molybdenum and molybdenum rhenium alloys do not lead to cytotoxicity in human and mouse fibroblasts. We also examined the degradation behavior of molybdenum by carrying out long-term immersion tests (up to 6 months) with molybdenum sheet metal. We showed that molybdenum has sufficient mechanical stability over at least 6 months for implants on the one hand and is subject to very uniform degradation on the other. The results of our experiments are very promising for the development of new resorbable osteosynthesis materials for craniomaxillofacial surgery based on molybdenum.

This study investigates the delubrication, reduction, and decarburization processes of powder metallurgical steel alloys (CrM, CrL, AHC, Mo85, SintD 35) and an unalloyed steel during sintering in a pure hydrogen atmosphere. Utilizing in-situ FTIR gas phase analysis, components with ethylenebisstearamide (EBS) as a lubricant are analyzed. EBS decomposition in steel components yields CO, CO₂, H₂O, and CH₄, with dominant CH groups observed in the 230 °C to 480 °C range. In the temperature range between 750 °C and 850 °C, where CO formation is expected due to the reduction of surface iron oxides, CH₄ is present instead, indicating that an “internal getter effect” also occurs in pre-alloyed powders. In addition, with high carbon activity, the reduction of internal iron oxides and the reduction of chromium oxides also trigger an internal getter effect. Depending on the carbon potential, these processes cause a considerable reduction in the carbon content of the powder metallurgical components. The study therefore shows that the decarburization of powder metallurgical components during the heat treatment phases prior to sintering in a 100 pct hydrogen atmosphere is less due to the mechanism of delubrication, but rather to mechanisms of carbothermal reduction.

The article investigates the development of a manufacturing route for highly porous titanium foams suitable for craniofacial surgery applications, particularly in cranioplasties. The study focuses on the polyurethane replication method for foam production and emphasizes reducing residual gas content, as it significantly affects the mechanical properties and suitability for approval of the foams. Various factors such as starting materials, solvent debinding, heating schedules, and hydrogen atmosphere are analyzed for their impact on residual gas content. It is shown that significant reductions in residual gas content can only be achieved by reworking each step of the process. A combination of initial solvent debinding of the PU template with dimethyl sulphoxide, reduction of suspension additives, use of coarser Gd. 1 powders, and an integrated debinding and sintering process under partial hydrogen atmosphere achieves a significant reduction in residual gas content. This way, the potential for producing titanium foams that comply with relevant standards for craniofacial implants is demonstrated.