Aim: To evaluate the hypothesis of a correlation between the preoperative residual alveolar bone height (RBH) and graft maturation after maxillary sinus floor augmentation procedures using two different bone substitutes. Methods: A total of 20 patients who underwent unilateral maxillary sinus floor augmentation with either mineralized deproteinized bovine bone (DBBM) or a xenograft enriched with polymer and gelatin (NBS) were included in this prospective study. Six months after sinus surgery, bone biopsies were harvested with a 3.2 mm diameter trephine bur, prior to dental implant placement. Histomorphometric analysis was performed, and the results were correlated with the individual RBH. Implants were loaded after 5 months of insertion, and 1-year implant success and marginal bone level change were assessed. Results: RBH was 2.17 ± 1.11 mm (range 0.5–3.5 mm) and 2.14 ± 0.72 mm (range 0.5–3.0 mm) in the NBS and DBBM group, respectively. The biopsy analyses for the DBBM group showed woven bone increases by 5.08% per 1-mm increment of RBH; medullary spaces decreased by 9.02%, osteoid decreased by 4.4%, residual biomaterial decreased by 0.34%, and lamellar bone increased by 5.68% per 1-mm increase of RBH. In the NBS group, samples showed woven bone increases by 8.08% per 1-mm increase of RBH; medullary spaces decreased by 0.38%; osteoid increased by 1.34%, residual biomaterial decreased by 0.58%, and lamellar bone decreased by 5.50% per 1-mm increase of RBH. There was no statistically significant difference in the correlation between RBH and lamellar bone, woven bone, and osteoid, independently of the material used. Implant success was 100% in both groups, and marginal bone loss was 1.02 ± 0.42 mm in DBBM and 0.95 ± 0.31 mm in the NBS group after the 1-year follow-up. Conclusion: In spite of the absence of significance, the observed trend for woven bone to increase and medullary spaces to decrease when RBH increases deserves attention. Residual bone dimension might be a determinant in the bone graft maturation after maxillary sinus augmentation.

Background: Due to the lack of data comparing the biological behavior of two formulations, granules and paste, of alloplastic graft from microtomographic and histomorphometric points of view, the aim of the present experiment was to compare the histomorphometric and microtomographic healing of two formulations, i.e., granules (MR sites) or paste (MR-inject sites) of an alloplastic graft composed of a combination of beta-tricalcium phosphate and hydroxyapatite used for maxillary sinus lifting. Methods: A sinus lifting procedure was carried out bilaterally in 20 rabbits, and the elevated space was filled with either paste or granules of an alloplastic material. A collagen membrane was placed on the antrostomy and the animals were euthanized after 2 or 10 weeks, 10 animals each group. Microtomographic and histological analyses were performed. Results: Higher proportions of new bone formation were found at the MR, compared to the MR-inject sites both after 2 weeks (2.65 ± 2.89% vs. 0.08 ± 0.12%; p < 0.01) and 10 weeks of healing (34.20 ± 13.86 vs. 23.28 ± 10.35%; p = 0.022). Conclusions: It was concluded that new bone formation was faster in the MR sites, compared to the MR-inject. However, a longer time of healing should be allowed to make final conclusions about the efficiency in bone formation of the paste formulation of the biomaterial used in the present study.