Freckle defects usually appear on the surface of castings and industrial ingots during the directional solidification process and most of them are located near the interface between the shell mold and superalloys. Ceramic cores create more interfaces in the directionally solidified (DS) and single crystal (SX) hollow turbine blades. In order to investigate the location of freckle occurrence in superalloys, superalloy CM247 LC was directionally solidified in an industrial-sized Bridgman furnace. Instead of ceramic cores, Alumina tubes were used inside of the casting specimens. It was found that freckles occur not only on the casting external surfaces, but also appear near the internal interfaces between the ceramic core and superalloys. Meanwhile, the size, initial position, and area of freckle were investigated in various diameters of the specimens. The initial position of the freckle chain reduces when the diameter of the rods increase. Freckle area follows a linear relationship in various diameters and the average freckle fraction is 1.1% of cross sectional area of casting specimens. The flow of liquid metal near the interfaces was stronger than that in the interdendritic region in the mushy zone, and explained why freckle tends to occur on the outer or inner surfaces of castings. This new phenomenon suggests that freckles are more likely to occur on the outer or inner surfaces of the hollow turbine blades.

A new heat conductor (HC) technique was developed to minimise stray grain formation arising from the geometrical effect during single crystal solidification of superalloys. Graphite is recommended as HC material because of its excellent thermophysical properties. Computer simulation and temperature measurements have shown that this technique is able to produce a clear improvement of thermal condition in the critical region of the components. Both the extent and the period of undercooling at the platform extremity significantly decreased. Structural investigation revealed a notable reduction in stray grain quota, providing evidence for the effectiveness of the HC technique for improving the quality of single crystal components.