Alloplasts are synthetic, inorganic, biocompatible bone substitutes that function as defect fillers to repair skeletal defects. The acceptance of these substitutes by host tissues is determined by the pore diameter and the porosity and inter-connectivity. This narrative review appraises recent developments, characterization, and biological performance of different synthetic materials for bone, periodontal, and dental tissue regeneration. They include calcium phosphate cements and their variants β-tricalcium phosphate (β-TCP) ceramics and biphasic calcium phosphates (hydroxyapatite (HA) and β-TCP ceramics), calcium sulfate, bioactive glasses and polymer-based bone substitutes which include variants of polycaprolactone. In summary, the search for synthetic bone substitutes remains elusive with calcium compounds providing the best synthetic substitute. The combination of calcium sulphate and β-TCP provides improved handling of the materials, dispensing with the need for a traditional membrane in guided bone regeneration. Evidence is supportive of improved angiogenesis at the recipient sites. One such product, (EthOss^® Regeneration, Silesden, UK) has won numerous awards internationally as a commercial success. Bioglasses and polymers, which have been used as medical devices, are still in the experimental stage for dental application. Polycaprolactone-TCP, one of the products in this category is currently undergoing further randomized clinical trials as a 3D socket preservation filler. These aforementioned products may have vast potential for substituting human/animal-based bone grafts.

Bioactive alloplastic materials, like beta-tricalcium phosphate (β-TCP) and calcium sulfate (CS), have been extensively researched and are currently used in orthopedic and dental bone regenerative procedures. The purpose of this study was to compare the performance of EthOss versus a bovine xenograft and spontaneous healing. The grafting materials were implanted in standardized 8 mm circular bicortical bone defects in rabbit calvariae. A third similar defect in each animal was left empty for natural healing. Six male rabbits were used. After eight weeks of healing, the animals were euthanized and the bone tissue was analyzed using histology and micro-computed tomography (micro-CT). Defects treated with β-TCP/CS showed the greatest bone regeneration and graft resorption, although differences between groups were not statistically significant. At sites that healed spontaneously, the trabecular number was lower (p < 0.05) and trabecular separation was higher (p < 0.05), compared to sites treated with β-TCP/CS or xenograft. Trabecular thickness was higher at sites treated with the bovine xenograft (p < 0.05) compared to sites filled with β-TCP/CS or sites that healed spontaneously. In conclusion, the novel β-TCP/CS grafting material performed well as a bioactive and biomimetic alloplastic bone substitute when used in cranial defects in this animal model.

Purpose.To present a novel protocol for alveolar bone regeneration in parallel to early implant placement.Methods.497 patients in need of extraction and early implant placement with simultaneous bone augmentation were treated in a period of 10 years. In all patients the same specific method was followed and grafting was performed utilizingin situhardening fully resorbable alloplastic grafting materials consisting ofβ-tricalcium phosphate and calcium sulfate. The protocol involved atraumatic extraction, implant placement after 4 weeks with simultaneous bone augmentation, and loading of the implant 12 weeks after placement and grafting. Follow-up periods ranged from 6 months to 10 years (mean of 4 years).Results.A total of 601 postextraction sites were rehabilitated in 497 patients utilizing the novel protocol. Three implants failed before loading and three implants failed one year after loading, leaving an overall survival rate of99.0%.Conclusions.This standardized protocol allows successful long-term functional results regarding alveolar bone regeneration and implant rehabilitation. The concept of placing the implant 4 weeks after extraction, augmenting the bone around the implant utilizing fully resorbable, biomechanically stable, alloplastic materials, and loading the implant at 12 weeks seems to offer advantages when compared with traditional treatment modalities.

This case report highlights the use of a novel in situ hardening synthetic (alloplastic), resorbable, bone grafting material composed of beta tricalcium phosphate and calcium sulfate, for alveolar ridge preservation. A 35-year-old female patient was referred by her general dentist for extraction of the mandibular right first molar and rehabilitation of the site with a dental implant. The nonrestorable tooth was “atraumatically” extracted without raising a flap, and the socket was immediately grafted with the synthetic biomaterial and covered with a hemostatic fleece. No membrane was used, and the site was left uncovered without obtaining primary closure, in order to heal by secondary intention. After 12 weeks, the architecture of the ridge was preserved, and clinical observation revealed excellent soft tissue healing without loss of attached gingiva. At reentry for placement of the implant, a bone core biopsy was obtained, and primary implant stability was measured by final seating torque and resonance frequency analysis. Histological analysis revealed pronounced bone regeneration while high levels of primary implant stability were recorded. The implant was successfully loaded 12 weeks after placement. Clinical and radiological follow-up examination at two years revealed stable and successful results regarding biological, functional, and esthetic parameters.

The purpose of this study was to investigate the effectiveness of a resorbable alloplastic in situ hardening bone grafting material for alveolar ridge preservation in a swine model. Seven Landrace pigs were used. In each animal, the maxillary left and right deciduous second molars were extracted, and extraction sites were either grafted with a resorbable alloplastic in situ hardening bone substitute, composed of beta-tricalcium phosphate (β-TCP) granules coated with poly(lactic-co-glycolic) acid (PLGA), or left unfilled to heal spontaneously. Animals were euthanized after 12 weeks, and the bone tissue was analyzed histologically and histomorphometrically. Linear changes of ridge width were also clinically measured and analyzed. Pronounced bone regeneration was found in both experimental and control sites, with no statistically significant differences. At the experimental sites, most of the alloplastic grafting material was resorbed and remnants of the graft particles were severely decreased in size. Moreover, experimental sites showed, in a statistically nonsignificant way, less mean horizontal dimensional reduction of the alveolar ridge (7.69%) compared to the control sites (8.86%). In conclusion, the β-TCP/PLGA biomaterial performed well as a biocompatible resorbable in situ hardening bone substitute when placed in intact extraction sockets in this animal model.

Frequently, sinus augmentation is required when replacing failing or missing molars in the maxilla due to loss of alveolar bone related to periodontal disease, pneumatization of the sinus or a combination of the two factors. Various materials have been advocated and utilized; these fall into the categories of allograft, xenograft and synthetic materials. This article shall discuss a study of 10 cases with a 2-year follow-up utilizing a novel synthetic graft material used for sinus augmentation either simultaneously with implant placement or in preparation for sinus augmentation and implant placement in the posterior maxilla. The results of the 10 cases in the study found consistent results over the 2-year study period with maintenance of the alveolar height at the maxillary sinus. A lack of complications or failures in the study group demonstrates the technique has useful applications in increasing ridge height to permit implant placement inferior to the sinus floor.