The paper is devoted to the study of the mechanical, microstructural, and bio-corrosive behavior of low-alloyed Zn–Mg biodegradable surgical wires for bone reconstructions. Three biodegradable alloys with different magnesium content have been studied, their production technology has been developed and the product properties have been determined. The technology includes casting, extrusion, hot and cold drawing of the wire, and the product surface finishing. The paper shows the most important stages of the process (i.e., extrusion and drawing) in detail. The technological parameters have been selected based on the results of the computer modeling. The flow stress–strain curves of extruded materials have been obtained at various strain rates and temperatures. Two drawing technologies have been compared. The first one is the room temperature conventional wire drawing. In the second one, the first few passes have been made at an elevated temperature and the rest at room temperature. This allowed avoiding the breaking of the wire during the first passes (a typical issue of the conventional technology for these alloys) and increasing the ductility of the final product. Mechanical properties, bio-corrosion, and crystallographic texture of the material were determined at different stages of the processing. A simultaneous increase in the wire strength, the number of repeated bending until the rupture of the wire, and in the bio-corrosion rate due to drawing has been registered. This phenomenon coincided with a change in the crystallographic texture. It has been shown that the product tensile strength of about 250–300 MPa can be reduced by about 30% due to surgical knots tied on it.

The study presents the results of research on the influence of different contents of main alloying additions, such as Mg (2 ÷ 2.5 wt.%), Cu (1.2 ÷ 1.9 wt.%), and Zn (5.5 ÷ 8 wt.%), on the strength properties and plasticity of selected Al–Zn–Mg–Cu alloys extruded on a bridge die. The test material variants were based on the EN AW-7075 alloy. The research specimens, in the form of 100 mm extrusion billets obtained with the DC casting method, were homogenized and extrusion welded during direct extrusion on a 5 MN horizontal press. A 60 × 6 mm die cross-section was used, with one bridge arranged in a way to extrude a flat bar with a weld along its entire length. The obtained materials in the F and T6 tempers were characterized in terms of their strength properties, hardness, and microstructure, using EBSD and SEM. The extrusion welding process did not significantly affect the properties of the tested materials; the measured differences in the yield strength and tensile strength between the materials, with and without the welding seam, were up to ±5%, regardless of chemical composition. A decrease in plasticity was observed with an increase in the content of the alloying elements. The highest strength properties in the T6 temper were achieved for the alloy with the highest content of alloying elements (10.47 wt.%), both welded and solid. Significant differences in the microstructure between the welded and solid material in the T6 temper were observed.

The extrusion of hollow profiles from hard-deformable AlZnMg alloys by using porthole dies encounters great technological difficulties in practice. High extrusion force accompanies the technological process, which is caused by high deformation resistance and high friction resistance in extrusion conditions. As a result of high thermo-mechanical loads affecting the die, a significant loss of dimensional accuracy of extruded profiles can be observed. The different projects of porthole dies for the extrusion of Ø50 × 2 mm tubes from the 7021 alloy were numerically calculated and then tested in industrial conditions by using a press of 25 MN capacity equipped with a container with a diameter of 7 inches (for 7021 alloy and 6082 alloy for comparison). New extrusion die 3 with modified bridge and mandrel geometry and a special radial–convex entry to the die opening was proposed. FEM was applied to analyse the metal flow during extrusion, geometrical stability of extruded tubes and the die deflection. The photogrammetric measuring method was used to evaluate dimensional accuracy of tubes extruded in different conditions and geometrical deviations in porthole dies elements, especially the bridges and the mandrels. Research revealed a high dimensional accuracy of tubes extruded from the 6082 alloy and from the 7021 alloy by using original extrusion die 3, while much higher dimensional deviations were noted for tubes extruded from the 7021 alloy by using extrusion dies 1 and 2, particularly in relation to the circularity, centricity and wall thickness.

The object of this study was to develop parameter of the die forging process, such as feedstock temperature and to investigate her impact on the structure and mechanical properties of magnesium alloys in different heat treatment conditions. Tests were carried out on a 2,5MN maximum capacity vertical hydraulic press using forgings of sample (model) shapes. Then, based on the results obtained in previous work, research was carried out to develop for items forged from magnesium alloys the parameters of heat treatment to the T5 and T6 condition in the context of achieving possibly homogeneous and fine-grained structure and, consequently, high mechanical properties.