The study presents the results of research on the influence of different contents of main alloying additions, such as Mg (2 ÷ 2.5 wt.%), Cu (1.2 ÷ 1.9 wt.%), and Zn (5.5 ÷ 8 wt.%), on the strength properties and plasticity of selected Al–Zn–Mg–Cu alloys extruded on a bridge die. The test material variants were based on the EN AW-7075 alloy. The research specimens, in the form of 100 mm extrusion billets obtained with the DC casting method, were homogenized and extrusion welded during direct extrusion on a 5 MN horizontal press. A 60 × 6 mm die cross-section was used, with one bridge arranged in a way to extrude a flat bar with a weld along its entire length. The obtained materials in the F and T6 tempers were characterized in terms of their strength properties, hardness, and microstructure, using EBSD and SEM. The extrusion welding process did not significantly affect the properties of the tested materials; the measured differences in the yield strength and tensile strength between the materials, with and without the welding seam, were up to ±5%, regardless of chemical composition. A decrease in plasticity was observed with an increase in the content of the alloying elements. The highest strength properties in the T6 temper were achieved for the alloy with the highest content of alloying elements (10.47 wt.%), both welded and solid. Significant differences in the microstructure between the welded and solid material in the T6 temper were observed.

Designing new aluminium alloys always requires an assessment of the influence of modified contents of the main alloying additions on the required properties for a specific application. The aim of this study was to develop a new alloy with a higher tensile strength than the tensile strength obtained in typical 6xxx series alloys, with a satisfactory hot extrusion ductility. The article presents the results of studies on the influence of copper additions, in three variants, on the structure and mechanical properties of extruded aluminium profiles in various heat treatment states. The base reference for the presented studies was the following aluminium alloys: AlMgSi (EN AW-6063) and AlCuMgMn (EN AW-2017). On this basis, three alloy variants with Cu contents of 2.5, 3.5 and 4.5 weight % were selected. These alloys were cast by vertical semi-continuous casting in the form of ingots with a diameter of 100 mm. Hot deformation studies were carried out in the process of co-extrusion on a semi-industrial line consisting of a horizontal 5 MN press together with auxiliary devices. The extruded profiles were free from defects that could have resulted from the process, such as overheating, cracks and blisters. The materials in the form of extruded profiles, in the heat treatment states T1 and T4, were characterised in terms of structure and mechanical properties. The variants with Cu contents of 2.5 wt% and 3.5 wt% had comparable structure and grain size, and the variant with 4.5 wt% Cu had a finer microstructure. For the studied alloys after heat treatment, higher the strength, higher the Cu content in the alloy, ranging from 445 to 543 MPa. It has been found that it is possible to develop modified aluminium alloys based on the 6xxx series with an increased copper addition (but still below the content typical for Al alloys of the 2xxx series) that will have a strength above 400 MPa. The first variant of the new alloy with a Cu content of 2.5 wt% meets the set goal and meets the requirements set at the beginning of the studies.

This study presents the results of research on the influence of different contents of copper in aluminium alloys based on the 6xxx series on mechanical and structural properties. The investigation started with the alloying, and casting four billet variants with different copper content—0.8% Cu; 2B—1% Cu; 3A—1.2% Cu; and 3B—1.4% Cu. The prepared materials were homogenised and extruded on a 500T horizontal press with two different process temperatures and ram speeds ranging from 1 mm/s to 9 mm/s. After heat treating to the T6 and T5 tempers, their mechanical properties were tested. On this basis, the two most promising alloys 2A and 3B were selected and subjected to further tests. After extrusion and heat treatment of the profiles (to F, T1, T2, T5, and T5510), their mechanical properties were determined to select the preferred process parameters. Finally, a structural test based on crystallographic orientation based on the EBSD technique and TEM observations allowed for the characterisation of grain size, dispersoids, and phase analysis. Bright-field (BF) analysis allowed us to compare the deformed areas for T1, T5, and T5510 temperatures. The results showed significant growth in the mechanical properties of all the subjected alloys, and the best properties were shown for a Cu content of 1.4% with a tensile strength of 460 MPa and an elongation of 16% (T5510 tempering). The structural test showed an average grain size of 18 µm to 23 µm and solid solution decomposition differences for different heat-treating parameters.

FEM numerical analyses can be indicated as a common and basic tool used in the design of processes based on the plastic forming of metals. In such simulations, the accuracy of the results strongly depends on the quality of the material constitutive data used as the input. Good understanding of metals and their alloys’ deformation behavior, especially at hot working temperatures, is the key to developing or optimizing proper and economical processes. To provide reliable FEM simulation results, it is crucial to select an appropriate experimental method describing material behavior at elevated deformation temperatures. The most commonly method used for this is hot torsion tests, which can effectively provide a basis for developing constitutive models (for example, the Hensel–Spittel equation), but also produce the material constants needed to fully describe the behavior of the metal. This paper analyzes three experimental methods, compression testing, torsion testing, and spherical probe pressing, for determining material flow stress characteristics required for FEM simulations. The study focuses on the EN AW-7075 alloy, a high-strength aluminum alloy with limited hot workability. The methods were validated by comparing FEM predictions of extrusion force and profile temperature with results from industrial extrusion trials conducted on a 5 MN horizontal press.