Monodispersed CuO octahedral crystals were successfully synthesized using a low-temperature co-precipitation method. Zinc doping in CuO created surface defects that enhanced oxygen adsorption on the surface crucial for gas sensing applications. Pure and Zn-doped CuO sensor films were realized using the doctor blade method. The sensor films showed selective response towards a low concentration of NO₂ at a lower operating temperature of 150 °C. Doping with Zn causes the resistance of the sensor film to decrease due to the enhancement of charge carriers with an analogous improvement in the sensor response. The observed decrease in sensor resistance agreed well with the findings of the work function studies. Zinc doping resulted in an increase in work function by 180 meV which, after NO₂ exposure, was found to increase by a further 130 meV, attributed to the oxidizing behavior of the test gas.

We report Ag nanoparticles infused with mesosphere TiO₂/reduced graphene oxide (rGO) nanosheet (TiO₂/rGO/Ag) hybrid nanostructures have been successfully fabricated using a series of solution process synthesis routes and an in-situ growth method. The prepared hybrid nanostructure is utilized for the fabrication of photovoltaic cells and the photocatalytic degradation of pollutants. The photovoltaic characteristics of a dye-sensitized solar cell (DSSC) device with plasmonic hybrid nanostructure (TiO₂/rGO/Ag) photoanode achieved a highest short-circuit current density (J_SC) of 16.05 mA/cm², an open circuit voltage (V_OC) of 0.74 V and a fill factor (FF) of 62.5%. The fabricated plasmonic DSSC device exhibited a maximum power conversion efficiency (PCE) of 7.27%, which is almost 1.7 times higher than the TiO₂-based DSSC (4.10%). For the photocatalytic degradation of pollutants, the prepared TiO₂/rGO/Ag photocatalyst exhibited superior photodegradation of methylene blue (MB) dye molecules at around 93% and the mineralization of total organic compounds (TOC) by 80% in aqueous solution after 160 min under continuous irradiation with natural sunlight. Moreover, the enhanced performance of the DSSC device and the MB dye degradation exhibited by the hybrid nanostructures are more associated with their high surface area. Therefore, the proposed plasmonic hybrid nanostructure system is a further development for photovoltaics and environmental remediation applications.